Abstract:Moisture absorption and dimensional distortion are the major drawbacks of wood utilization as building material. In this study, poplar wood coated with a thin layer of titanium dioxide (TiO2) was prepared by the cosolvent-controlled hydrothermal method. Subsequently, its moisture absorption and dimensional stability were examined. Scanning electron microscopy analysis revealed that the wood substrate was closely and entirely covered with the TiO2 coat. Microscale features were visible despite masking of the ultrastructural features of the cell wall. To explore the effects of TiO2 coating on the water-repellency and dimensional stability of wood, a 90-day water immersion test was carried out. Results showed that water absorption and thickness swelling of TiO2-coated wood increase very slowly and minimally. Weight change after 90 days of water immersion was reduced to 20.5%, nearly one-tenth of untreated control wood, and that maximum cross-sectional relative swelling was only 1.2%. Specimens were conditioned for 3 months at 20%, 30%, 40%, 50%, 60%, 70%, 80%, and 90% relative humidity (RH) to determine the effects of RH on moisture absorption and dimensional swelling of TiO2-coated wood. There was no change in weight after 3 months of being exposed to humidity conditions below 60%, whereas there was linear weight increase above 60% RH, but the maximum change was less than 6%. Cross-sectional relative swelling was less than 0.3% below 60% RH but increased as RH exceeded 60%. The maximum change was approximately 3%. Anisotropic thickness swelling of wood was almost eliminated after coating. It is obvious that TiO2 coating can act as a moisture barrier for wood and is an exceptionally strong water vapor-inhibiting shield under very humid conditions.

Effect of Titanium Dioxide on Color Stability and Mildewproof Properties of Bamboo

Effect Of Titanium Dioxide On The Uv-C Ageing Behavior Of Silicone Rubber

Study on Nano- Titanium Dioxide Thin Film Coated on Self-cleaning Glass Surface

Room Temperature Synthesis of Crystalline Anatase TiO2 on Bamboo Timber Surface and Their Short-Term Antifungal Capability under Natural Weather Conditions

UV Resistant Properties of Composite Modiifed Nano Titanium Dioxide and Its Application

Improvement of Water Resistance and Dimensional Stability of Wood Through Titanium Dioxide Coating

The Effect of Antibacterial and Waterproof Coating Prepared From Hexadecyltrimethoxysilane and Nano-Titanium Dioxide on Wood Properties

Enhanced Ultraviolet Shielding Performances of TiO₂ Nanorods in Different Crystalline Structures and Illite-Loaded Composites

Enhanced Ability of Nanostructured Titania Film to Assist Photodegradation of Rhodamine B in Water Through Natural Aging

Photocatalytic degradation of selected dyes by titania thin films with various nanostructures

Surface Functionalization of Cellulose Fibers with Titanium Dioxide Nanoparticles and Their Combined Bactericidal Activities

Surface property enhancement of bamboo by inorganic materials coating with extended functional applications

Surface Modification of Titanium Dioxide and Photocatalytic Activity of Its Coating Film

Boron-Based Mildew Preventive and Ultraviolet Absorbent Modification of Waterborne Polyurethane Coatings on Laminated Bamboo

Surface Morphology and Modulus, Wetting Behavior and Photocatalytic Activity of the TiO2 Coated Materials Based on PMMA/O-MMT Composite Microfibers

Improvement in hygroscopicity and dimensional stability of bamboo through a synthetic modification of maleic anhydride with tung oil heat treatment

Mechanical, dynamic mechanical and thermal properties of TiO2 nanoparticles treatment bamboo fiber-reinforced polypropylene composites

Multi-Scale Evaluation of the Effect of Thermal Modification on Chemical Components, Dimensional Stability, and Anti-Mildew Properties of Moso Bamboo

Performance and mechanism of antibacterial activity and organic dyes degradation of WO3/TiO2/(Ca,Y)F2:Tm,Yb loaded on Bio-CaCO3

Effects of Substrates Made of Noncrystal and Polycrystal on Photocatalytic Degradation of Basic Crystal Violet

Effect of Titanium Dioxide Nanoparticles on the Properties of Poly(Vinyl Alcohol)/Silica Hybrid Films Prepared by the Sol-Gel Method