Abstract:A kind of hydrophobic silica with good dispersibility was prepared first. The silica and epoxy natural rubber (ENR) were blended in Haake internal mixer at high temperature in a powerful shear force filed, and so the grafted silica was made through in-situ grafting reaction between the hydroxyl groups of silica and the epoxy groups of ENR. The grafting processes were performed as follows: first, the silica should be dried about 24 h at 100 degrees C in an oven to remove the free water molecules that absorbed on the surface of silica. Secondly, the grafting reaction temperature was chosen at 170 degrees C that confirmed by the test result of a Monsanto MDR-2000 moving die rheometer, and the weight proportions between silica and ENR were chosen to be 1: 1, 2: 1 and 3: 1 separately in this study. Thirdly, ENR was mixed in HAAKE internal mixer about I min, then silica was added to react with the ENR for another 15 min before discharged, and the outputs named ENR-grafted silica were obtained as we wanted. In order to obtain an appropriate grafting condition, the effect of different weight proportions between silica and ENR on the stress-strain curves of natural rubber composites reinforced by the grafted silica was discussed. Through analyses of the reinforcement effect, the appropriate proportion between silica and ENR was chosen to be 3: 1. FTIR, TGA and TEM analysis results indicated that ENR was successfully grafted onto the silica surface. FTIR result of the grafted silica showed the new absorptions. The peaks at 2966,2929 and 2862 cm(-1) are assigned to CH stretching vibrations. The absorption band at 1660 cm(-1) is characteristic of C C stretching. The stretching vibration of epoxy groups that should be at 870 cm-' was missing, suggesting the epoxy groups were almost used up to react with silanol groups. A new shoulder peak appears at 3640 cm(-1), which is ascribed to - 011 stretching of C-OH which is the result of the reaction of silanol groups and ENR. TGA curves revealed ENR grafted silica showed a new step between 348 - 449 degrees C due to the decomposition of ENR, and the grafting rate reached 21.3 %. TEM images indicated the size of silica agglomerates became small obviously after modification because of the grafting layer preventing the silica particles from conglomerating. Then, compared with the silica without grafting, the properties of NR composites filled with grafted silica were investigated. The "Payne effect" results indicated that the grafted ENR molecules reduced the silica-silica interaction by enhancing the rubber-silica interaction, and so the grafted silica had better dispersibility in natural rubber ( NR) composites. Mechanical properties test of NR composites proved that the grafted silica could more effectively improve the reinforcement effect due to the strong interface combination between silica and ENR. DMA results showed that the temperature of glassy transition of ENR bound to the silica surface shifted to higher temperatures. Consequently, the composite contained the grafted silica had high strength and high hysteresis at the same time on the normal temperature. So the composites have potential application in the shocking absorber products, the tire of racing cars, and so on.

Synthesis and Characterization of Natural Rubber Grafted with 2-Hydroxyethyl Methacrylate

Simultaneous Graft Polymerization of Polypropylene with Maleic Anhydride and Butyl Acrylate

Studies on grafting kinetics of bulk copolymerization of styrene onto rubber(I) - Grafting behavior

Modification of Natural Rubber Latex by Graft Copolymerization of 2-Ethylhexyl Acrylate and Methacrylic Acid

Synthesis and characterization of poly(vinyl chloride)-g-poly (2-hydroxyethyl methacrylate) copolymers

Effect of silane coupling agent grafted glycidyl methacrylate on hollow microsphere/natural rubber composites

Research Progress in Modification of Natural Rubber Via Graft Copolymerization

Preparation and Properties of High Performance Bio-based Elastomer Based on Methyl Methacrylate Grafted Natural Rubber

Characterization of chemical structure and morphology of MCS graft terpolymer

PREPARATION AND CHARACTERIZATION OF THE NATURAL RUBBER COMPOSITES REINFORCED BY EPOXY NATURAL RUBBER GRAFTED SILICA WITH GOOD DISPERSIBILITY

Structure and Properties of Natural Rubber-Organoclay Nanocomposites Prepared by Grafting and Intercalating Method in Latex

Preparation and Characterization of Graft Copolymer EVA-g-PU

Study on Solution Polymerization of EPDM-g-MS by Grafting Method

A Novel Grafting‐modified Waste Rubber Powder As Filler in Natural Rubber Vulcanizates

Effect of complex of resorcinol and hexamethylenetetramine modified halloysite nanotubes (RH-HNTs) on the mechanical and swelling characteristics of NR/EPDM nanocomposites

Ternary-Monomer Solid Phase Graft Copolymers of Polyethylene by Solid Phase Graft Copolymerization

"Preparation and Water-Swelling Properties of Grafted Natural Rubber Based Water-Swellable Rubber"

Synthesis of EPDM-g-PMMA through atom transfer radical polymerization

Synthesis and characterization of graft copolymer hydrogel by “grafting from” atom transfer radical polymerization using brominated macro monomeric initiator and investigation of hydrogel properties

Preparation and mechanical properties of water‐dispersible hyperbranched polymer grafted carbon black/natural rubber composites by latex blending method

Preparation of Starch- G -PMMA, Starch- G -P(MMA/BMA) and Starch- G -P(MMA/MA) Nanoparticles and Their Reinforcing Effect on Natural Rubber by Latex Blending: a Comparative Study