Abstract:The auxo-action of ZrC particles to ferrite grain refining during deformation induced ferrite transformation of the tested steel was investigated by unidirectional compression thermal simulating experiment with Gleeble-1500.The results show that the ZrC particles which radius less-than 1.0 μm as a deformation and recrystallization nucleus can accelerate ferrite nucleating thus refine ferrite grain,and in order to improve α-Fe nucleating rate,the critical volume fraction of ZrC particles is 0.6% which leads to the ultrafine microstructure of the tested steel.When the rolling deformation is 60% and the volume fraction of ZrC particles is 0.5% the fine structure with a grain size of 3~4 μm was obtained,tensile strength was improved 70 percent approximately,and the integrating mechanical properties of the steel are increased obviously.

Study of Strengthening Low-Carbon Microalloy Steel by Adding Ultrafine Second-Phase Particles