Effect of Ph on the Crystalline Structure and Degradation Property of Acetylated Starch Film

LI Xiao-xi,HUANG Chen,PENG Xu,CHEN Ling,YU Long,LI Lin

2012-01-01

Abstract:In order to investigate the degradation property of acetylated starch film in simulated environments with different pH,acetylated starch film was installed in the different simulated environments with different pH as 1.2,7,12,respectively.The weight loss rate,surface morphology,crystalline structure,hydrophobic property and mechanical property were characterized and analyzed by SEM,XRD,contact angle measurement,mechanical testing and DMA.The results showed that the structure and mechanical property of acetylated starch film were affected by the different values of pH.During the degradation,the V-type crystalline structure of the film was kept and the hydrophobic property and elongation at break decreased while the tensile strength decreased after an initial increase.Under the alkaline condition,the degradation rate of the film was much higher in the initial 14 days and the surface defect was partially appeared and the crystallinity increased as the degradation time increased.In contrast,under the acid condition,the film degradated more quickly in later stage and the holes were appeared on the surface of the film and the crystallinity increased before decreasing from the 28th day.These results provided fundamental data for the development of the starch-based degradable materials with different degradation rate which were suitable for different application environment.