Influence of high concentration dimethylsulfoxide on the ultrastructure and biomechanical characteristics of patellar tendon allografts

沈灏,蒋垚,程海涛,王慧敏

DOI: https://doi.org/10.3969/j.issn.0253-9934.2001.09.007

2001-01-01

Abstract:Objective To study the biomechanical property and ultrastructure of the patellar tendon allografts treated with high concentration dimethylsulfoxide(DMSO) before and shortly after transplantation and the relation between them. Methods The bone patellar tendon-bone grafts were taken from New Zealand rabbits and divided into the fresh frozen (FF) group, in which the grafts were directly frozen and stored in -80℃, and the test group, in which the specimens were incubated in 65% DMSO before being deeply frozen and kept in -80 ℃. Three to five weeks later, the allografts were implanted into rabbits' right knees to reconstruct the anterior cruciate ligaments (ACLs). Histological change, ultrastructure pattern and biomechanical property were observed 0 week, 3 weeks and 6 weeks after transplantation. Results Histologically, in the DMSO group the PTs showed a relatively compact collagen arrangement shortly after transplantation. Ultrastructurally, the diameter and interfibrillar space of the collagen fibrils in the DMSO treated grafts were similar to those in the normal PTs before transplntation, but in the frash frozen grafts the diameter of the collagen fibrils was obviously increased (200 nm) and the interfibrillar space enlarged. The biomechanical strength of PT in the DMSO group was stronger than that in the FF group before, and 6 weeks after transplntation. Conclusion Treating allografts with high concentration dimethylsulfoxide is in favour of keeping their collagen matrix stability and maintaining biomechanical property.