Mechanical Property Analysis of PVA/HA Composite Hydrogel and Its Finite Element Simulation

DAI Zu-ming,ZHANG De-kun,CHEN Kai

DOI: https://doi.org/10.16156/j.1004-7220.2012.03.021

2012-01-01

Abstract:Objective To study the effect from the content change in hydroxyapatite(HA) on mechanical properties of polyvinyl alcohol/hydroxyapatite(PVA/HA)composite hydrogel and its load bearing characteristics based on experiment and finite element simulation.Methods The compression and stress relaxation tests of PVA/HA composite hydrogel were performed on the UMT test machine.Through the simulation and experimental results,the load-bearing characteristics of PVA/HA composite hydrogel and the effect of HA on PVA/HA composite hydrogel performance were investigated.Results With HA content increasing,the compression modulus of PVA/HA composite hydrogel was first increased and then decreased,while its permeability coefficient was first decreased and then increased.When the HA content was 3%,the compression modulus of PVA/HA composite hy-drogel reached maximum(1.25 MPa)and its permeability coefficient reached minimum(1.59×10-3 mm4 · N-1 · s-1).The fluid bearing proportion of PVA/HA composite hydrogel was first increased and then decreased with the loading time increasing,which presented a nonlinear change.The proportion of the fluid bearing was significantly increased after HA added into PVA / HA composite hydrogel.The stress relaxation rate was first increased and then decreased with HA content increasing.Under the same loaded displacement,PVA / HA composite hydrogel with 3% HA content could disperse more contact stress.Conclusions The internal bearing characteristics of PVA / HA composite hydrogel have a great impact on its mechanical properties.When the HA content is 3%,the PVA / HA composite hydrogel has the best mechanical properties,which are closer to those of the natural articular cartilage.