Abstract:Purpose At present, the conventional method of preparing cationic fluorinated acrylic latex is to emulsify copolymerised monomers with cationic surfactants. However, there has been a wide concern about using Gemini surfactants to prepare cationic polymer latex to improve its properties. The purpose of this paper was to focus on the synthesis of novel self-crosslinked cationic fluorinated acrylic latex (SCFAL), during which the copolymerised monomers were initiated with a water soluble azo initiator and emulsified with mixed surfactants of Gemini emulsifier and alkyl polyglycoside (APG). Design/methodology/approach The novel SCFAL was prepared successfully by the semi-continuous seeded emulsion polymerisation of butyl acrylate, methyl methacrylate, hexafluorobutyl methacrylate (HFMA) and hydroxy propyl methacrylate (HPMA) in aqueous medium. Findings The conversion is the maximum and the coagulation percentage the minimum when the amounts of emulsifier and initiator are 8 and 0.6 per cent, respectively. The average particle size of the latex is significantly reduced with the increase of the amount of emulsifiers used. However, the average particle size of the latex is increased with the increase of the amount of HPMA. The particle size of the latex is of a unimodal distribution, which means that the particle size was reasonably uniform. Contact angle is increased with the increase of the amount of the HFMA. Practical implications The novel SCFAL can be widely used as significant components in the field of coatings, leather, textile, paper, adhesives and so on. Originality/value SCFAL, which was emulsified with novel mixed surfactants of Gemini surfactant and APG, has been prepared successfully. Influences of amount of initiator, emulsifier, HPMA and HFMA on emulsion polymerisation and/or properties of novel latex are investigated in detail.

Synthesis of Acrylate Emulsion Modified by Self-cross Linking Organic Silicon

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Study on Silicone Modified Polyurethane-Acrylate Copolymer Emulstion

Synthesis and properties of alkoxysilane-modified acrylic latex via miniemulsion polymerization

Preparation and characterization of self-crosslinking acrylate emulsion modified by divinyl silane

Synthetic methods of acrylate polymer latexes modified with organosilicons and their film properties

Synthesis of Self-Stratifying Polyacrylate Latex Containing Silicon

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO₂ and Fluorine

Preparation and properties of ambient self-crosslinking acrylic emulsion

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Synthesis of a novel siloxane-based crosslink agent and its application in emulsion copolymerization of butyl acrylate and methyl methacrylate

Core-Shell Emulsion Copolymerization and Characterization of Polysiloxane Bearing Vinylic Function/Acrylate Monomer

Preparation and Thermal Stability of Phosphorus Acrylic Latex Modified with Organic Silicon

Synthesis and Characterization of Core-shell Organosiloxane Modified Acrylate Latex

Synthesis and Characterization of Nano-silica/Polyacrylate Composite Emulsions by Sol-gel Method and In-Situ Emulsion Polymerization

Synthesis and Properties of Poly-Acrylate Emulsion Modified by Organ Silicone

Synthesis and Properties of Novel Self-Crosslinked Cationic Fluorinated Acrylic Latex Prepared with Novel Emulsified System

Preparation and properties of Versatate-acrylate emulsion modified by organic silicon

Silicone Acrylic Emulsion Coatings

A Novel Approach to Graft Acrylates Onto Commercial Silicones for Release Film Fabrications by Two-Step Emulsion Synthesis

Synthesis and Characterization of Novel Acrylate Emulsion Containing Phosphorus and Silicon Prepared Via Semi-Continuous Seeded Emulsion Polymerization