Efficient Organic Photovoltaics Using Solution-Processed, Annealing-Free TiO2 Nanocrystalline Particles As an Interface Modification Layer
Jian Xiong,Bingchu Yang,Jun Yuan,Ling Fan,Xu Hu,Haipeng Xie,Lu Lyu,Ruili Cui,Yingping Zou,Conghua Zhou,Dongmei Niu,Yongli Gao,Junliang Yang
DOI: https://doi.org/10.1016/j.orgel.2014.12.023
IF: 3.868
2015-01-01
Organic Electronics
Abstract:A solution-processed, annealing-free TiO2 nanocrystalline particles (TiO2 NPs) as an interface modification layer was inserted in organic photovoltaics (OPVs), in which the widely used polymer poly (3-hexyl thiophene) (P3HT), a low band gap alkoxylphenyl substituted [1,2-b:4,5-b′] dithiophene-based polymer (PBDTPO-DTBO), and a soluble small molecule benzodithiophene derivative (TIBDT) were used as the donor material, respectively. The annealing-free TiO2 NPs could be easily spin-coated upon the surface of organic active layers, and showed comparable properties to thermal-annealed ones. The power conversion efficiencies (PCEs) of OPV devices could be enhanced dramatically with inserting an annealing-free TiO2 NPs layer. The PCEs of OPV devices based on P3HT:PC61BM, PBDTPO-DTBO:PC71BM and TIBDT:PC61BM bulk heterojunctions were improved by 28%, 15% and 27%, respectively, with an annealing-free TiO2 NPs layer, in which the highest PCE of 5.76% was achieved in PBDTPO-DTBO:PC71BM OPVs. The solution-processed, annealing-free TiO2 NPs thin films show great potential applications in the fabrication of large-area OPVs by printing or coating techniques on flexible polymer substrates. In particularly, it would promote to fabricate solution-processed, annealing-free OPV devices with suitable hole transport layer and organic/polymer active materials.