Abstract:Abstract Mesoporous Y zeolites were prepared by the sequential chemical dealumination (using chelating agents such as ethylenediaminetetraacetic acid, H 4 EDTA, and citric acid aqueous solutions) and alkaline desilication (using sodium hydroxide, NaOH, aqueous solutions) treatments. Specifically, the ultrasound-assisted alkaline treatment (i.e., ultrasonic treatment) was proposed as the alternative to conventional alkaline treatments which are performed under hydrothermal conditions. In comparison with the hydrothermal alkaline treatment, the ultrasonic treatment showed the comparatively enhanced efficiency (with the reduced treatment time, i.e., 5 min vs. 30 min, all with 0.2 mol·L −1 NaOH at 65°C) in treating the deal-uminated Y zeolites for creating mesoporosity. For example, after the treatment of a dealuminated zeolite Y (using 0.1 mol·L −1 H4EDTA at 100°C for 6 h), the ultrasonic treatment produced the mesoporous zeolite Y with the specific external surface area ( S external ) of 160 m 2 ·g· −1 and mesopore volume ( V meso ) of 0.22 cm 3 ·g −1 , being slightly higher than that by the conventional method (i.e., S extemal = 128 m 2 ·g −1 and V meso = 0.19 cm 3 ·g −1 ). The acidic property and catalytic activity (in catalytic cracking of n -octane) of mesoporous Y zeolites obtained by the two methods were comparable. The ultrasonic desilication treatment was found to be generic, also being effective to treat the dealuminated Y zeolites by citric acid. Additionally, the first step of chemical dealumination treatment was crucial to enable the effective creation of mesopores in the parent Y zeolite (with a silicon-to-aluminium ratio, Si/Al = 2.6) regardless of the subsequent alkaline desilication treatment (i.e., ultrasonic or hydrothermal). Therefore, appropriate selection of the condition of the chemical dealumination treatment based on the property of parent zeolites, such as Si/Al ratio and crystallinity, is important for making mesoporous zeolites effectively.

Preparation of Y Zeolite Composites with Adjustable, Highly Dispersed Intra-Crystal Mesoporosity: Effect of Lactic Acid Treatment in CTAB-assisted Two-Step Approach

Continuous Synthesis of Mesoporous Y Zeolites from Normal Inorganic Aluminosilicates and Their High Adsorption Capacity for Dibenzothiophene (DBT) and 4,6-Dimethyldibenzothiophene (4,6-DMDBT)

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Y and ZSM-5 Hierarchical Zeolites Prepared Using a Surfactant-Mediated Strategy: Effect of the Treatment Conditions

Sequential Microwave-Assisted Dealumination and Hydrothermal Alkaline Treatments of Y Zeolite for Preparing Hierarchical Mesoporous Zeolite Catalysts

Synthesis and Post-synthesis Modification of Zeolite Y for Improved Methanol Adsorption and Coke Formation Resistance

Synthesis, characterization and influence parameters on the overgrowth of micro/mesoporous Y-zeolite-MCM-41 composite material under acidic conditions

Nano-crystallite Oriented Self-Assembled ZSM-5 Zeolite and Its LDPE Cracking Properties: Effects of Accessibility and Strength of Acid Sites

Tailor and Control of Acidic Strength in Ordered Mesoporous Aluminosilicates by Using Preformed Zeolite Precursors

Facile Morphology and Porosity Regulation of Zeolite ZSM-5 Mesocrystals with Synergistically Enhanced Catalytic Activity and Shape Selectivity

Understanding Of The Dissolution-Crystallization Fabrication Strategy Towards Macro/Microporous Zsm-5 Single Crystals

Hierarchical Zeolites Prepared Using a Surfactant-Mediated Strategy: ZSM-5 vs. Y as Catalysts for Friedel–Crafts Acylation Reaction

Preparation of a Hierarchical Pore Zeolite with High-Temperature Calcination and Acid-Base Leaching

Impact of Synthesis Parameters on the Crystallinity of Macroscopic Zeolite Y Spheres Shaped Using Resin Hard Templates

Tailoring the pore structure、morphology and acidity of MFI zeolites by the regulation of Si/Al ratio in the synthetic gel

Facile synthesis of hierarchical porous ZSM-5 zeolite with tunable mesostructure and its application in catalytic cracking of LDPE

Insight into the construction of multi-cavity micro-mesoporous SSZ-13: Dissolution, Al backfilling and framework reconstruction

Hierarchical submicrosized Y zeolites prepared by sequential desilication-dealumination post-synthesis modification and their catalytic performance in vacuum gas oil hydrocracking.

Using ultrasound to improve the sequential post-synthesis modification method for making mesoporous Y zeolites

The effect of hierarchical single-crystal ZSM-5 zeolites with different Si/Al ratios on its pore structure and catalytic performance

A Comparative Study on Mesoporous Y Zeolites Prepared by Hard-Templating and Post-Synthetic Treatment Methods