Structure and Magnetic Properties of Pr2Fe17−xMnx (x=0–9) Compounds

ZG Sun,HW Zhang,JY Wang,BG Shen
DOI: https://doi.org/10.1063/1.371492
IF: 2.877
1999-01-01
Journal of Applied Physics
Abstract:The influence of Mn substitution for Fe on the structure and magnetic properties of Pr2Fe17−xMnx compounds with 0⩽x⩽9 was investigated. X-ray diffraction indicates that all samples are single phase with the rhombohedral Th2Zn17-type structure. The unit cell volume V remains nearly constant with increasing manganese content up to x=2, then increases linearly at a rate of about 2.5 Å3 per Mn atom up to x=8 and there is a large increase of cell volume at x=9. The Curie temperature increases a little from 298 K at x=0 to 308 K at x=1, and then decreases to 37 K at x=9 quickly. The saturation magnetization at 5 K was found to decrease monotonously with increasing Mn concentration. The thermal magnetization curves M(T) of the compounds with x=1–9 show a strong decrease below TC with decreasing temperature. Also it presents considerable magnetic hardness at low temperature. This can be attributed to the presence of narrow Bloch walls.
What problem does this paper attempt to address?