Abstract:The practical applications of magnetocaloric materials for magnetic refrigeration require not only large magnitude but also reversibility, as well as room-temperature operating temperature, of the magneto caloric effect. However, it is a complex problem to simultaneously meet these demands in the Heusler-type Ni-(Co)-Mn-X (X = In, Sn, Sb, Ga) magnetic shape memory alloys which are a promising candidate for magnetocaloric materials, owing to the interdependence of magnetostructural transformation parameters. Here, through synergic tuning of magnetostructural transformation parameters via alloying with Ti in Ni42-xTixCo9Mn39Sn10 alloys, we achieved a large reversible room-temperature magnetocaloric effect. By alloying with a proper amount of Ti, the martensitic transformation temperature was brought down to room temperature and the sensitivity of transformation temperature to magnetic field change was greatly enhanced with the transformation entropy change still remaining a large value, while the thermal hysteresis and the transformation interval only slightly increased. Thus, the field required to induce the complete and reversible transformation was significantly reduced. As a result, a large reversible room-temperature magnetic entropy change Delta S-m of 18.7 J kg(-1) K-1 under 5 T was achieved in the Ni41Ti1Co9Mn39Sn10 alloy. This is the first report on reversible Delta S-m in Ni-Mn-Sn-based Heusler alloys and the Delta S-m we achieved represents the highest reversible Delta S-m under 5 T reported heretofore in Ni-Mn-based Heusler alloys. Furthermore, the Ni41Ti1Co9Mn39Sn10 alloy shows good compressive properties and stable martensitic transformation during thermal cycling, beneficial for potential magnetocaloric applications. This study is instructive for the development of high-performance magnetocaloric materials for room-temperature magnetic refrigeration. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Large Successive Magnetocaloric Effects Around Room Temperature in Ni 50 Mn 34 in 15 Al Alloy

Large Field-Induced Magnetocaloric Effect in Ni<formula formulatype="inline"><tex Notation="TeX">$_{43}$</tex> </formula>Mn<formula formulatype="inline"><tex Notation="TeX">$_{46 - {\rm x}}$</tex></formula>V<formula formulatype="inline"><tex Notation="TeX">$_{\rm x}$</tex></formula>Sn<formula formul

Large Field-Induced Magnetocaloric Effect in Ni$_{43}$Mn$_{46 - {\rm X}}$v$_{\rm X}$sn$_{11}$ Heusler Alloys

Comnsb: A Magnetocaloric Material with A Large Low-Field Magnetic Entropy Change at Intermediate Temperature

Magnetocaloric Effect with Low Magnetic Hysteresis Loss in Ferromagnetic Ni-Mn-Sb-Si Alloys

Large Refrigeration Capacity in a Ni42Co8Mn37.7In12.3 Magnetocaloric Alloy

Giant room-temperature inverse and conventional magnetocaloric effects in Ni–Mn–In alloys

Giant Magnetic Refrigeration Capacity Near Room Temperature in Ni40Co10Mn40Sn10 Multifunctional Alloy

Large Reversible Magnetocaloric Effect in a Ni-Co-Mn-In Magnetic Shape Memory Alloy

Enhanced Magnetic Entropy Change and Working Temperature Interval in Ni–Mn–In–Co Alloys

Large Low-Field Magnetocaloric Effect in a Directionally Solidified Ni 50 Mn 18 Cu 7 Cu 25 Alloy

Giant and Reversible Room-Temperature Magnetocaloric Effect in Ti-Doped Ni-Co-Mn-Sn Magnetic Shape Memory Alloys

Cyclic Reversible Martensitic Transformation and Magnetocaloric Effect in a Ni51.0Mn20.8Ga22.4Cu5.8 Alloy

Large Magnetic Entropy Changes In The Ni45.4mn41.5in13.1 Ferromagnetic Shape Memory Alloy

Large Refrigeration Capacity in a Ni48Co1Mn37In14 Polycrystalline Alloy with Low Thermal Hysteresis

Simultaneously Achieved Large Reversible Elastocaloric and Magnetocaloric Effects and Their Coupling in a Magnetic Shape Memory Alloy

Large Magnetocaloric Effect at Low Magnetic Field in Ni50−xCoxMn35In15 Ribbons

Effect of Partial Metamagnetic and Magnetic Transition Coupling on the Magnetocaloric Effect of Ni-Mn-Sn-Fe Alloy

Understanding of the giant magnetic entropy change around the co-occurrence point of martensitic and magnetic transitions in Ni-Mn-In Heusler alloy

Large Magnetic Entropy Change and Refrigeration Capacity Around Room Temperature in Quinary Ni41Co9-xFexMn40Sn10 Alloys (x= 2.0 and 2.5)

Large Magnetocaloric and Magnetoresistance Effects During Martensitic Transformation in Heusler-type Ni44Co6Mn37In13 Alloy