Abstract:The photo-enhanced dissolution of semiconducting birnessite by organic reductants prevalently occurs in the euphotic zones of natural aquatic systems. However, the underlying photoelectrons transfer mechanisms and kinetic factors are not fully understood. In this study, the anoxic photoreduction of delta-MnO2 (a phase analogue for natural birnessite) by citrate under simulated solar irradiation at pH 4.0, 5.5 and 7.0 was investigated, and the structural evolution of delta-MnO2 during the reaction was examined. The photoreduction of delta-MnO2 was observed at all three pHs. similar to 86.0% and similar to 32.7% Mn2+ was released into the solution at pH 4.0 and 5.5, respectively; while negligible amount of dissolved Mn2+ was produced at pH 7.0. Mn average oxidation state (AOS) in both the bulk and surface of delta-MnO2 lowered significantly with decreasing pH (3.39/2.56, 3.57/3.07 and 3.78/3.19 in bulk/surface at pH 4.0, 5.5 and 7.0, respectively). The increase in the photoreduction rate and extent of 8-MnO2 at lower pHs indicated the photoelectron transfer was pH-dependent. From the amount of reduced Mn(III/II) in structure and Mn2+ in solution, the average photoelectron transfer amount per mol Mn was calculated as 1.81, 0.95 and 0.22 at pH 4.0, 5.5 and 7.0, respectively. The retention of Mn(II) (-13% in content) in the structure of reacted delta-MnO2 was only observed at pH 4.0 rather than higher pHs. The photoreduction of Mn(IV) involved two successive steps of single-electron transfer to produce Mn(III) and further Mn(II), and the above results suggested the second-step photoelectron transfer was more effective under acidic conditions. The potential difference between the conduction band (CB) and MnO2/Mn2+ half-reaction was enlarged as pH decreased, which conduced to the optimal effectiveness of photoelectron transfer and thorough reduction of Mn(IV/III) under lower pH conditions. The pH-dependent Mn photoreduction occurred throughout the structure of delta-MnO2, whereas for the dark reaction, the influence of pH on the reduction extent only took effect on the surface. These observations implied the dark-reaction electron transfer predominantly occurred at the surface sites. By contrast, according to the semiconductor energy band theory, the excited CB photoelectrons were shared by all atoms in the lattice of delta-MnO2, and each Mn atom had equal chance to be reduced by photoelectrons. Furthermore, the accumulation of photo-reduced and large-size Mn(III/II) in the layer caused the spatial expansion of the in-plane crystallization, and could possibly alter the layer symmetry or even promote the long-term structural transformation towards tunneled Mn oxides. This work provides insights into the photocatalytic geochemical performance of the naturally-abundant birnessite, which is influenced by varied pH conditions on Earth's surface.

Effective Zinc Adsorption Driven by Electrochemical Redox Reactions of Birnessite Nanosheets Generated by Solar Photochemistry

Electrochemistry of rechargeable aqueous zinc/zinc-sulphate/manganese-oxide batteries and methods for preparation of high-performance cathodes

K-buserite manganese oxide nanosheets enabling high-efficiency energy storage in aqueous Zn-ion batteries and hybrid supercapacitors

High-Performance Aqueous Zinc–Manganese Battery with Reversible Mn2+/Mn4+ Double Redox Achieved by Carbon Coated MnOx Nanoparticles

Uncovering sulfur doping effect in MnO2 nanosheets as an efficient cathode for aqueous zinc ion battery

Sodium Ion Pre-Intercalation of δ-MnO2 Nanosheets for High Energy Density Aqueous Zinc-Ion Batteries

Ultrathin Δ-Mno2 Nanoflakes with Na+ Intercalation As a High-Capacity Cathode for Aqueous Zinc-Ion Batteries

The Controlled Synthesis of Birnessite Nanoflowers Via H2O2 Reducing KMnO4 for Efficient Adsorption and Photooxidation Activity

Structural Directed Growth of Ultrathin Parallel Birnessite on Β-Mno2 for High-Performance Asymmetric Supercapacitors.

Mechanochemical reactions of MnO<sub>2</sub> and graphite nanosheets as a durable zinc ion battery cathode

Interface regulated MnO2/Mn2+ redox chemistry in aqueous Zn ion batteries

Effect of 1-1 electrolyte concentration on the adsorption/desorption of copper ion on synthetic birnessite

The adsorption mechanism of Zn 2+ by triclinic birnessite and the mechanism

Mechanochemical reactions of MnO2 and graphite nanosheets as a durable zinc ion battery cathode

Interfacial Synthesis of Strongly-Coupled Δ-Mno2/mxene Heteronanosheets for Stable Zinc Ion Batteries with Zn2+-exclusive Storage Mechanism

Ultrafine Nano-Network Structured Bacterial Cellulose As Reductant and Bridging Ligands to Fabricate Ultrathin K-birnessite Type MnO2 Nanosheets for Supercapacitors

Photo-stimulated Anoxic Reduction of Birnessite (Δ-Mno2) by Citrate and Its Fine Structural Responses: Insights on a Proton-Promoted Photoelectron Transfer Process

Manipulating Ion Concentration to Boost Two‐Electron Mn4+/Mn2+ Redox Kinetics Through a Colloid Electrolyte for High‐Capacity Zinc Batteries

A High-Energy and Long-Life Aqueous Zn/Birnessite Battery Via Reversible Water and Zn2+ Coinsertion.

Performance Study of Bimetallic Mn-Zn Porous Flower-Like Nanosheets As Supercapacitor Positive Electrode Materials

Effect of Electrolyte on Adsorption/Desorption of Cu<Superscript>2+</Superscript> on Nano-particle Mn Oxide