Mechanical, Thermal and Combustion Properties of Intumescent Flame Retardant Biodegradable Poly (lactic Acid) Composites

Ning Zhang,Xiang Lu

DOI: https://doi.org/10.1080/14658011.2018.1534391

2018-01-01

Abstract:Despite extraordinary mechanical properties and excellent biodegradability, poly (lactic acid) (PLA) still suffers from a highly inherent flammability, restricting its applications in the electric and automobile fields. Although a wide range of flame retardants have been developed to reduce the flammability, they normally compromise the mechanical strength of PLA. In this study, a series of composites based on PLA, have been prepared by melt-blending with intumescent flame retardants (IFRs). The morphology, thermal stability and burning behaviour of the composites were investigated using a scanning electron microscope-energy dispersive spectrometer (SEM-EDS), thermogravimetric analysis (TGA), the limiting oxygen index (LOI), vertical burning (UL-94) and the cone calorimeter test (CCT). The LOI value reached 38.5% and UL-94 could pass V-0 for the PLA/IFR composite containing only 12 wt-% IFR. The dispersion of IFR in PLA was observed using SEM-EDS. A significant improvement in fire retardant performance was observed for the PLA/IFR composite from the CCT (reducing the heat release rate and the total heat release). More importantly, compared to pure PLA, the addition of IFR did not seriously deteriorate the mechanical properties of the material.