Evolution of Microstructure and Carbon Distribution During Heat Treatments of a Dual-Phase Steel: Modeling and Atom-Probe Tomography Experiments

Dong An,Sung-Il Baik,Shiyan Pan,Mingfang Zhu,Dieter Isheim,Bruce W. Krakauer,David N. Seidman

DOI: https://doi.org/10.1007/s11661-018-4975-7

2018-01-01

Abstract:The temporal evolution of microstructures and carbon distributions in a Fe-0.323C-1.231Mn-0.849Si (mol pct) dual-phase steel during heat treatments are simulated using a two-dimensional cellular automaton model. The model involves austenite nucleation, phase transformations controlled by ferrite ( α )/austenite ( γ ) interface mobility and the local carbon concentration, and long-range carbon diffusion. It is also coupled with a solute drag model to account for the effect of substitutional elements on the interface migration. The results show that after holding at 800 °C for 300 seconds the transformed γ -volume fraction is lower than the paraequilibrium prediction. During subsequent cooling at 6 °C s −1 , the γ → α transformation takes place after a stagnant stage; the carbon concentrations in both the α - and γ -phases increase and become non-uniform. When cooled below 450 °C, the γ -volume fraction is nearly unchanged. A small amount of carbon enriched martensite, transformed from the remaining γ -phase, exists in the room temperature microstructure. The simulated microstructures and carbon concentrations in martensite compare reasonably well with the experimental micrographs and atom-probe tomographic measurements. During tempering at 400 °C, martensite decomposes and the carbon concentration in the α-matrix increases. The simulation results are used to understand the mechanisms of yield strength variations after different heat treatments.