Structures and Properties of Blown Moulding LLDPE Films
W. Yang,G. -F. Shan,X. -G. Tang,B. -H. Xie,Z. -M. Li,Q. -C. Zhou,M. -B. Yang
DOI: https://doi.org/10.1179/174328906x128252
2006-01-01
Abstract:The crystalline structures, mechanical properties, transparence and fracture behaviours of linear low density polyethylene blown moulding films with nucleating agents incorporated in were investigated. The results indicated that with the nucleating agents used, the melting temperature T m, crystalline structures, general profile of the stress–strain curves, tensile yield strength σ y and essential work of fracture parameters before yield of the films, were almost unchanged, while the strain hardening phenomenon, tensile fracture strength σ b, elongation at break &epsi b, transparence and fracture parameters w e and βw p were enhanced greatly. As the loading content of nucleating agent increasing, the crystallinity first decreased and then increased rapidly; the strain hardening phenomenon ϵ b and σ b increased to a maximum and then decrease to a stable value, while the T m and σ y were also unchanged; the haze decreased first and then reached a stable value; the w e and w e,y decreased remarkably first and then rapidly increased, even enormously exceeding the w e of pure linear low density polyethylene, while βw p and β y w p,y increased to a quite high value first and then dropped to a lower level.