Formation and investigation of dual cross-linked high temperature proton exchange membranes based on vinylimidazolium-functionalized poly(2,6-dimethyl-1,4-phenylene oxide) and polystyrene

Jingshuai Yang,Haoxing Jiang,Liping Gao,Jin Wang,Niya Ye,Yixin Xu,Ronghuan He
DOI: https://doi.org/10.1039/c8py01148f
IF: 4.6
2018-01-01
Polymer Chemistry
Abstract:A 1-decyl-2-methylimidazole (DMIm) functionalized poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) membrane is fabricated and employed to dope phosphoric acid (PA) for use as a high temperature proton exchange membrane. This kind of membrane displayed superior PA doping capability, but poor mechanical properties. In order to improve the dimensional and mechanical stabilities without sacrificing proton conductivities, a series of dual cross-linked membranes are prepared using the poly(styrene-vinylimidazole-divinylbenzene) (poly(St-VIm-DVB)) copolymer as a crosslinker. The reaction of vinylimidazole with benzyl bromide not only constructs a cross-linking network, but also endows the membranes with a PA doping capacity for proton conduction. The reticular polymer chain structure improves the mechanical properties of the membranes, especially at elevated temperatures. As an example, PPO-70%VIm-30%DMIm/180.1%PA achieves a high proton conductivity of 0.067 S cm(-1) at 180 degrees C without humidification, while it displays suitable tensile strengths of 5.0 MPa and 2.1 MPa at room temperature and 120 degrees C, respectively. These membranes show great potential for use as an electrolyte in high temperature proton exchange membrane fuel cells.
What problem does this paper attempt to address?