Abstract:The Ni-Al intermetallic sheets were prepared by the reaction synthesis of pure Ni and Al foils with different thickness ratios. The first stage was performed at 640 °C/20 MPa/6 h to consume Al layers, and the second stage was performed at 1200 °C/20 MPa/1 h to complete the synthesis of Ni-Al intermetallic sheets. The thickness ratios of original Ni and Al foils strongly affected the microstructure and mechanical properties of Ni-Al intermetallic sheets. When Ni/Al thickness ratio was 1:1.5 (R1:1.5), the microstructure was single-phase NiAl with bimodal grain structure, and it transformed into coarse grains dominated single-phase NiAl structure when Ni/Al thickness ratio was 1:1 (R1:1). The microstructures changed to NiAl+Ni3Al+Ni when the ratios were 1:0.63 (R1:0.63) and 1:0.25 (R1:0.25). At ambient temperature, Samples R1:0.25 and R1:0.63 had high strength, while Samples R1:1 and R1:1.5 showed serious brittleness. At high temperature, Sample R1:1 showed preferable ductility with the elongation of 61.3%, 71.4% and 101.3% at 800 °C, 900 °C and 1000 °C, respectively; Sample R1:0.63 showed the highest tensile strength, with the values of 350.3 MPa, 230.5 MPa and 140.2 MPa at 800 °C, 900 °C and 1000 °C, respectively. For the fracture at ambient temperature, Sample R1:0.25 showed a mixed fracture mode of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mainly cleavage fracture; Sample R1:1 showed a typical brittle cleavage fracture with a large number of river-like patterns; the fracture mode of Sample R1:1.5 was brittle transgranular fracture for coarse grain layers (CGLs) and intergranular fracture for fine grain layers (FGLs). At high temperature, Samples R1:1.5 and R1:1 were mixed fracture modes of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mixed quasi-cleavage and cleavage fracture; the fracture mode of Sample R1:0.25 was single cleavage fracture with microcracks at the NiAl layers.

Al3Ni Alloy Synthesized at High Pressures and Its Debye Temperature

The Effects of High Pressure and Superheating on the Planar Growth of Al3Ni Phase in Hypo-Peritectic Al-30wt%Ni Alloy

Study on the Phase Selection and Debye Temperature of Hyper-Peritectic Al-Ni Alloy under High Pressure

First-principles Study of Ni-Al Intermetallic Compounds under Various Temperature and Pressure

The Formation of Bulk Β-Al3ni Phase in Eutectic Al-5.69wt%Ni Alloy Solidified under High Pressure

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

The Microstructure Evolution and Mass Transfer in Mushy Zone During High-Pressure Solidifying Hypoeutectic Al-Ni Alloy

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

The microstructure and mechanical properties of reaction synthesized Ni-Al intermetallic sheets by pure Ni/Al foils with different thickness ratios

Microstructure and solidification behaviour of Ni3Al/Ni7Hf2 eutectic alloy

Microstructure Evolution of Directionally Solidified Al-12%Ni Hypereutectic Alloy

Investigating the Influence of Al Contents on Microstructure and Mechanical Properties of Ni 3 Al Superalloy Fabricated by Twin Wire‐Based Direct Arc Energy Deposition

Microstructure and formation mechanism of Ni-Al intermetallic compounds fabricated by reaction synthesis

Synthesis of Nb3Al high temperature intermetallic compound by laser deposition

Microstructure and Mechanical Properties of Ni3Al and Ni3Al–1B Alloys Fabricated by SHS/HE

Microstructure and mechanical properties of a novel polycrystalline Ni3Al-based intermetallic alloy

Characterization of Ni3Al Alloy Fabricated by Thermal Explosion and Hot Extrusion Process

Superplasticity of a directionally solidified NiAl–Fe(Nb) alloy at high temperature

L1 2 nanoparticle-strengthened CoNi-based superalloy with ultrahigh yield stress developed using CALPHAD method

Solidification Behaviors of Undercooled Ni-P Alloys

Microstructure and Mechanical Properties of Ni3Al Fabricated by Thermal Explosion and Hot Extrusion