Abstract:The increasing interest in decreasing the surface defects of sprayed Ca-P coating deposited on carbon/carbon (C/C) composites to enhance the bonding strength, bioactivity and corrosion resistance of the coating is justified by the growing evidence of its beneficial effect on the bone replacement fields. Microwave-hydrothermal (MH) method detailed in the previous study is successfully used to reduce the above coating defects and the MH mechanism is well studied here. Hence, five different treatment reagents involving calcium and phosphorus solution, sulfuric acid (H2SO4) solution, ammonium hydroxide (NH3·H2O) solution, only Ca2+ solution and deionized water are selected as the precursor solution. The surface, cross-sectional morphologies, phase and composition of the coatings are characterized by the scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), microscopy Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) spectra. Elastic modulus and coating hardness are measured by nanoindentation. Results reveal that the presence of calcium and phosphorus ions, as well as the H2SO4 in the precursor solution during the MH process, have a positive influence on the reduction of sprayed Ca-P coating surface defects. However, the coating treated by other three solutions cannot produce new phases on the basis of sprayed Ca-P coating and the surface defects of it are not decreased. Nevertheless, the elastic modulus and hardness of the coating treated by H2SO4 solution are very weak. MH treated coating by calcium and phosphorus ions in the precursor solution and in NH3·H2O solution, only Ca2+ solution and deionized water own the similar elastic modulus and hardness to that of the sprayed Ca-P coating. To conclude, in the MH process, the surface defects of the sprayed Ca-P coating are only lowered in calcium and phosphorus precursor solution and the coating strength is not dropped, which demonstrates the promoting mechanism of MH process.

Microwave-hydrothermal Method Post-Treatment of Sprayed Ca-P Coating

Surface Defects Repairing of Sprayed Ca-P Coating by the Microwave-Hydrothermal Method

Mechanical properties of the supersonic atmospheric plasma sprayed CaP coating post-processed by a microwave-hydrothermal method

Effect of the Heating Time on the Preferred Growth of Hydroxyapatite Crystal Prepared by Microwave-Hydrothermal Technique on the Defective Surface of Sprayed Coating

Microstructures, Mechanical Properties and Corrosion Resistance of Sprayed Ca–P Coating for Micropatterning Carbon/carbon Substrate Surface

Ca-P bioactive coating prepared by combining microwave-hydrothermal and supersonic atmospheric plasma spraying methods

Effect of sprayed techniques on the surface microstructure and in vitro behavior of nano-HAp coatings

Effect of Surface Pre-Treatments on the Formation and Degradation Behaviour of a Calcium Phosphate Coating on Pure Magnesium

Effect of Microwave Heating Time on Bonding Strength and Corrosion Resistance of Ca-P Composite Layers for Carbon/carbon Composites

Different Surface States of Carbon/carbon Substrate on the Sprayed Calcium Phosphate Coating Shear Strength

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

The influence of discharge power and heat treatment on calcium phosphate coatings prepared by RF magnetron sputtering deposition

The mechanical beheavior of plasma sprayed HA coating with different post-treaed way

Calcium Phosphorus Bio-Coating on Carbon/carbon Composites: Preparation, Shear Strength and Bioactivity

Microwave-Assisted Post-processing of Detonation Gun-Sprayed Coatings for Better Slurry and Cavitation Erosion Resistance

The Effect of Post-Treatment on the Mechanical Behavior of Plasma Sprayed HA Coating

Water Vapour-Treated Hydroxyapatite Coatings after Plasma Spraying and Their Characteristics

Effect of Thermal Treatment on Microplasma Sprayed HA Coating

Electric polarized post treatment of plasma sprayed hydroxyapatite coatings in alkaline solution

Preparation and corrosion behavior of calcium phosphate and hydroxyapatite conversion coatings on AM60 magnesium alloy

Immersion Behavior of Plasma-Sprayed Modified Hydroxyapatite Coatings after Heat Treatment