Abstract:Tungsten trioxide (WO3) is believed to be a promising electrode candidate for supercapacitors, due to its reversible surface redox reaction resulted from the almost same W-O bond lengths with different oxidation states. However, the specific capacitance of WO3 electrode is very low (< 250 mF cm(-2)) because of its low conductivity and slow surface redox reaction kinetics. Herein, to address these issues, mesoporous WO3 nanosheets with exposed (200) facets were anchored on activated carbon cloth (ACC) via a simple two-step process including heat treatment and alcohol-thermal process. The ACC was coated on WO3 seeds and proceed a heat treatment at 500 degrees C and the time of alcohol-thermal process were 7 h, 8 h, and 9 h labeled as WO3@ACC-n (n = 7, 8, 9). SEM and TEM images confirmed the WO3 nanosheets were successful anchored on the ACC. The WO3@ACC-8 electrode showed the best specific areal capacitance which could reach as high as 659 mF cm(-2) at a current density of 5 mA cm(-2) and superior stability with almost no decrease in 10,000 cycles in the presence of Na2SO4 as the neutral electrolyte. The capacitance is encouragingly much higher than the previously reported values in a three-electrode system in the neutral aqueous condition. DFT calculations reveal that, in comparison to the (002) and (020) facets, the exposed (200) facets of the mesoporous WO3 nanosheets triggers the superior Na+-adsorption, which accelerates the Na+-involved surface redox reaction for the boosted supercapacitor performance. A flexible asymmetric supercapacitor (FASC) was fabricated from the WO3@ACC electrode, which exhibits high energy density (0.5 mWh cm(-3)) and power density (62 mW cm(-3)) without any attenuation during +/- 180 degrees wide-angle bending.

Facile Preparation of WO3 Nano-Fibers with Super Large Aspect Ratio for High Performance Supercapacitor

Zeolitic Imidazolate Framework Derived ZnCo2O4 Hollow Tubular Nanofibers for Long-Life Supercapacitors

High-performance supercapacitors of Cu-based porous coordination polymer nanowires and the derived porous CuO nanotubes.

Simple Synthesis of 1D, 2D and 3D WO3 Nanostructures on Stainless Steel Substrate for High-Performance Supercapacitors

Facilely synthesized porous NiCo2O4 flowerlike nanostructure for high-rate supercapacitors

Facile Preparation of W5O14 Nanosheet Arrays with Large Crystal Channels As High-Performance Negative Electrode for Supercapacitor

Synthesis of Oxygen‐Deficient WO3−x Nanoplates and Hollow Microspheres Decorated on a Carbon Cloth for Supercapacitors

Synthesis of oxygen‐deficient WO3‐x nanoplates and hollow microspheres decorated on carbon cloth for supercapacitor

Facile fabrication 1D/2D/3D Co3O4 nanostructure in hydrothermal synthesis for enhanced supercapacitor performance

Formation of High-Performance Cu-WOx@C Tribasic Composite Electrode for Aqueous Symmetric Supercapacitor

3D nanoporous ZnWO4 nanoparticles with excellent electrochemical performances for supercapacitors

Organic-inorganic hybrid electrode engineering for high-performance asymmetric supercapacitor based on WO3-CeO2 nanowires with oxygen vacancies

Utilization Mild and Green Oxidation Method to Fabricate Skin-Core Structure Derived from Non Melting-Shrinkage PPS Carbon Fibers with Ultra-Thin Nanosheets for High Performance Asymmetric Supercapacitor

Triggering Superior Sodium Ion Adsorption on (2 0 0) Facet of Mesoporous WO3 Nanosheet Arrays for Enhanced Supercapacitance

Porous ZnO-Coated Co3O4 Nanorod as a High-Energy-Density Supercapacitor Material.

One-dimensional Zinc-Manganate Oxide Hollow Nanostructures with Enhanced Supercapacitor Performance.

Facile Synthesis of NiWO4/reduced Graphene Oxide Nanocomposite with Excellent Capacitive Performance for Supercapacitors

MnO2 Nanowires-Decorated Carbon Fiber Cloth As Electrodes for Aqueous Asymmetric Supercapacitor

Cu(I)/Cu(II) Partially Substituting the Co(II) of Spinel Co3O4 Nanowires with 3D Interconnected Architecture on Carbon Cloth for High-Performance Flexible Solid-State Supercapacitors

Facile Green Route to Ni/Co Oxide Nanoparticle Embedded 3D Graphitic Carbon Nanosheets for High Performance Hybrid Supercapacitor Devices

Carbon Cloth@t-Nb2o5@mno2: A Rational Exploration of Manganese Oxide for High Performance Supercapacitor