Highly Flexible and Large Areal/volumetric Capacitances for Asymmetric Supercapacitor Based on ZnCo2O4 Nanorods Arrays and Polypyrrole on Carbon Cloth As Binder-Free Electrodes

Xinming Wu,Lian Meng,Qiguan Wang,Wenzhi Zhang,Yan Wang

DOI: https://doi.org/10.1016/j.matlet.2018.09.053

IF: 3

2019-01-01

Materials Letters

Abstract:Flexible asymmetric supercapacitor (FAS), as a promising candidate for wearable or flexible electronic devices, draws great attention since it exhibits the flexibility and enhanced areal/volumetric capacitances comparing with the symmetrical Faraday capacitors. Herein, we grow unique ZnCo2O4 nanorods arrays on carbon cloth (ZnCo2O4-CF) by a simple hydrothermal method, and the electrode exhibits a remarkable areal (volumetric) capacitance of 5.18 F cm(2) (167.5 F cm(3)) at 5 mA cm(2) and exceptional capacitance retention of 92.8% after 3000 cycles. A FAS was fabricated using ZnCo2O4-CF as the positive and PPy-CC (deposition of Polypyrrole on carbon cloth) as negative electrodes, respectively. Especially, the asymmetric electrodes help the device to exhibit a wide potential window of 1.6 V and a high areal (volumetric) capacitance of 1.8 F cm(2) (148 F cm(3)). As a result, the FAS shows a maximum energy of 2.3 mW h cm(2) (18.9 mW h cm(3)) at a power density of 7.82 mW cm(2) (82.2 mW cm(3)) and a good stability after 5000 cycles at a current density of 5.0 A cm(2). Furthermore, the FAS shows good flexibility and can withstand bending at different angles while keeping electrochemical performance constant. (C) 2018 Elsevier B.V. All rights reserved.