A Comparative Study of the Catalytic Oxidation of Chlorobenzene and Toluene over Ce-Mn Oxides

Yu Wang,Wei Deng,Yifu Wang,Limin Guo,Tatsumi Ishihara
DOI: https://doi.org/10.1016/j.mcat.2018.08.022
IF: 4.6
2018-01-01
Molecular Catalysis
Abstract:The morphology effects on the activity and stability of Ce-Mn oxide catalysts for chlorobenzene (CB) and toluene oxidation were compared and investigated in this work. Ce-Mn nano-sheets (CM S), nano-particles (CM-P) and nano-rods (CM-R) were firstly prepared. The obvious morphology effects on the reactions were observed: the activity for toluene oxidation followed the order of CM-S > CM-P > CM-R. In contrast, the activity for CB oxidation followed the order of CM R > CM-P > CM-S. For toluene oxidation, toluene adsorption and the C-H bond dissociation occurred at lower temperatures on the CM-S catalyst. The experimental results demonstrated that the higher content of surface adsorbed oxygen species and oxygen vacancies, as well as the enhanced 0(1att) species mobility of the CM-S catalyst were responsible for its highest catalytic activity. For CB oxidation, inactive planar CB adsorption on the 2D surface of CM-S catalyst and the strongly adsorbed Cl species from the CB decomposition resulted in serious deactivation of the catalyst. On the other hand, CB adsorption and the C-Cl bond dissociation occurred at lower temperatures on the CM R catalyst, Cl-contained species can be easily removed during the Deacon Reaction and gas phase oxygen can be adsorbed on the CM-R surface to replenish the consumed oxygen, resulting in the improved activity and stability. These results showed that the catalytic performance of Ce-Mn oxides for CB and toluene oxidation was greatly affected by their morphologies.
What problem does this paper attempt to address?