Abstract:Cracks that may cause pipeline cracking and leakage become the main risk of in-service pipelines after conventional metal loss defects have been detected. Therefore, it is imperative to develop ultra-high-definition magnetic flux leakage (MFL) detection for cracks. Due to the larger spatial sampling interval of conventional MFL inspections than the crack defect width, sparse sampling will result in problems such as missed detection of crack defects or insufficient signal sampling of crack defect MFL signals. To address the problem, this paper presents a detection topology in which the magnetic field signal is integrated first and then sampled, and it can effectively sample the leakage magnetic field of cracks. Furthermore, a magnetic field spatial integration (MFSI) method is proposed based on the magnetic dipole model, which develops an analytical solution for the depth quantification of crack defects. Using the multi-MFL spatial integral values under different lift offs, iterative equations are constructed, and the numerical solution for the width quantification of crack defects is provided. The finite element simulation and physical experiment are constructed. And, the results show that the proposed MFSI method can realize the quantification of crack size. When the crack defect aspect ratio is greater than 4, the quantization error of the crack depth and width does not exceed 0.7 mm and 0.1 mm, respectively. The robustness of the MFSI method for crack quantification is also discussed and verified. Moreover, based on theoretical analysis and simulation data, this paper concludes that the distribution of cracks MFL signal is width-insensitive, which would cause that classic MFL opening profile recognition methods for metal loss defects are no longer applicable to crack defects. Therefore, the proposed MFSI method is useful and meaningful for crack defect quantification in ultra-high-definition MFL detection.

Quantitative MFL Testing Technique for Strand Rope Based on a Small Number of Discontinuity Samples

Quantitative Nondestructive Testing of Wire Ropes Based on Features Fusion of Magnetic Image and Infrared Image

Adaptive Multi-Scale Bayesian Framework for MFL Inspection of Steel Wire Ropes

Extraction of weak signal based on wire rope detection in timing belt of wind turbines

Research on 3D MFL testing of wire rope based on empirical wavelet transform and SRCNN

Wire Rope Defect Recognition Method Based on MFL Signal Analysis and 1D-CNNs

Numerical Simulation on Magnetic Flux Leakage Testing of the Steel Cable at Different Speed Title

Quantitative Nondestructive Testing of Broken Wires for Wire Rope Based on Multi-Image Fusion

Improved Reconstruction of Magnetic Flux Leakage Signal From Wire Rope Damage Using Novel Smooth Function and Feature Peak Compensation

Nondestructive Testing of Wire Ropes Based on Image Fusion of Leakage Flux and Visible Light

A Novel Defect Quantification Method Utilizing Multi-Sensor Magnetic Flux Leakage Signal Fusion

Quantitative Study on MFL Signal of Pipeline Composite Defect Based on Improved Magnetic Charge Model

A Sensor for Broken Wire Detection of Steel Wire Ropes Based on the Magnetic Concentrating Principle

Quantitative Nondestructive Testing of Broken Wires for Wire Rope Based on Magnetic and Infrared Information

A Novel Crack Quantification Method for Ultra-High-Definition Magnetic Flux Leakage Detection in Pipeline Inspection

Accurate wire rope defect MFL detection using improved Hilbert transform and LSTM neural network

The Real-Time Quantitation and Display Method for Incomplete Defect MFL Signals

Quantitative Nondestructive Testing for Wire Rope Based on Multi-Source Information Fusion

Structure and Character Analysis of a New Type of Steel Wire Rope NDT Detector Apparatus

Experimental Analysis of the Magnetic Leakage Detection of a Corroded Steel Strand Due to Vibration

Quantification method of tubing defects based on machine learning algorithm and magnetic flux leakage signals