Bright Gradient-Alloyed CdSexS1–x Quantum Dots Exhibiting Cyan-Blue Emission
Jing Zhang,Qian Yang,Hong Cao,Christopher I. Ratcliffe,David Kingston,Queena Y. Chen,Jianying Ouyang,Xiaohua Wu,Donald M. Leek,Frank S. Riehle,Kui Yu
DOI: https://doi.org/10.1021/acs.chemmater.5b04380
IF: 10.508
2016-01-01
Chemistry of Materials
Abstract:Highly emissive alloyed CdSeS quantum dots (QDs) with a gradient structure exhibiting photoluminescence (PL) peaking at 490 um and an absolute quantum yield (QY) of 79% (in toluene with excitation wavelength of 430 nm) were designed and synthesized. The cyan-blue emitters were synthesized at 180 degrees C in 1-octadecene (ODE) with cadmium oleate (Cd(OA)(2)), tri-n-octylphosphine selenide (TOPSe), and tri-n-octylphosphine sulfide (TOPS) as the Cd, Se, and S precursors, respectively; importantly, a commercial secondary phosphine, diphenyl phosphine (DPP or HPPh2), was used as a beneficial additive. Also, our high Cd/(Se + 5) feed molar ratio aids in shifting the equilibrium of the chalcogenide exchange, TOPE + HPPh2 double left right arrow TOP + E=PPh2H, to the right. Density functional theory (DFT) calculations suggest that the formation of Se=PPh2H proceeds faster than that of S=PPh2H, which supports our high S/Se feed molar ratio used to synthesize the bright gradient-alloyed CdSeS QDs. Compositional and structural characterization was carried out using powder X-ray diffraction (PXRD), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS), and solid-state nuclear magnetic resonance spectroscopy (NMR). Particularly, our solid-state Cd-113 NMR analysis reveals that the highly emissive CdSeS QDs consist of a three-domain structure with a Se-rich inner core region, a Se/S equivalent middle region, and a S-rich outer region. The present study highlights the importance on the use of secondary phosphines together with high cation/anion feed molar ratios in the rational design and synthesis of high-quality metal chalcogenide QDs at relatively low temperature but with high yield and reproducibility.