Abstract:ZnS/CaZnOS:Mn 2+ luminescent ceramic components exhibit both photoluminescence (PL) and mechanoluminescence (ML). A PL material luminesces upon optical irradiation, whereas ML material converts mechanical energy into optical energy. ML materials have important application prospects in new light sources, damage detection, healthcare and anti-counterfeit encryption. In this paper, we report the preparation of luminescent ZnS/CaZnOS:Mn 2+ ceramic parts via vat photopolymerization 3D printing and discuss possible applications. We use manganese-doped zinc sulphide/zinc calcium oxysulfide powder as the raw luminescent ceramic powder and investigate the slurry preparation, vat photopolymerization 3D printing and sintering to fabricate photoluminescent and ML ceramic prototypes. The powder particle size was 9–10 μm, the coupling agent was 4 wt% silane (KH-570), and the photoinitiator was 2 wt% diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide. The result is a manganese-doped photosensitive slurry with uniform stability and fluidity, a solid content of 50 vol%, and a viscosity of 3 Pa·s. This slurry has excellent characteristics for vat photopolymerization 3D printing, with a penetration depth C d = 35.03 μm and a theoretical exposure energy E c = 2.26 mJ/cm 2 . ZnS/CaZnOS:Mn 2+ parts manufactured in this study exhibit both PL when irradiated by a light source and ML when extruded and rubbed. The photon intensity as high as 200 × 10 5 is released from ZnS/CaZnOS:Mn 2+ when irradiated at 339 nm, which is nearly 50% more than that released when irradiated at 290 nm. The intensity of ML photons emitted increases with the applied mechanical force, with up to 1700 intensity emitted. Conventional forming methods mainly involve coating parts with luminescent materials mixed with polydimethylsiloxane polymer, surrounding ZrO 2 cores by a shell layer of ML hybrid material and other traditional processes, which cannot produce complex structures or provide long-lasting luminescence. This study thus combines the luminescent material ZnS/CaZnOS:Mn 2+ and vat photopolymerization 3D printing to produce complex parts with low surface roughness (Sa = 5.92 μm and Sz = 53.11 μm before sintering, and Sa = 5.09 μm and Sz = 50.73 μm after sintering) and high chemical stability. These results expand the applications of ZnS/CaZnOS-based luminescent ceramic materials and vat photopolymerization 3D printing.

Three-dimensional Printing of Hybrid Organic/inorganic Composites with Long Persistence Luminescence

Novel AIE Luminescent Tetraphenylethene-Doped Poly (lactic Acid) Composites for Fused Deposition Modeling and Their Application in Fluorescent Analysis of 3D Printed Products

Tunable afterglow for mechanical self-monitoring 3D printing structures

Metal-Free organic polymeric room temperature phosphorescence system with Multi-Colour and ultralong lifetime

3D printing of multicolor luminescent glass

3D–printing AIE Stereolithography Resins with Real−time Monitored Printing Process to Fabricate Fluorescent Objects

Synthesis and Characterization of Stereolithography 3D Printing Fluorescent Resin

Visualization of photocuring and 4D printing with real-time phosphorescence

3D Printing of Resin Composites Doped with Upconversion Nanoparticles for Anti-Counterfeiting and Temperature Detection.

Fabrication of Translucent and Chemically Durable Crystal‐Glass Composite with Multicolor Persistent Luminescence

A Facile and Green Method to Prepare Highly Luminescent and Mechanically Robust Polylactide-Based Composites for Three-Dimensional Printing

Ultrastable and Colorful Afterglow from Organic Luminophores in Amorphous Nanocomposites: Advanced Anti-Counterfeiting and in Vivo Imaging Application

Unleashing the glow: upconverting nanoparticles recharge persistent luminescent materials – applications in 3D-printing and optical coding

Photopolymerization 3D Printing of Luminescent Ceramics

Upconversion 3D printing enables single-immersion multi-material stereolithography

Photoresponsive Luminescent Silica Nanoparticles as Additive for 3D Printing and Electrospinning

Two Are Better Than One: A Design Principle For Ultralong-Persistent Luminescence Of Pure Organics

Kilogram‐Scale Fabricated Organic Long‐Persistent Luminescence Materials with Multi‐Level Temperature Response

UV‐curing‐enhanced Organic Long‐Persistent Luminescence Materials

Chromaticity-Tunable All-Inorganic Color Converters Fabricated by 3D Printing for Modular Plant Growth Lighting Devices

Five-in-one: Dual-mode ultralong persistent luminescence with multiple responses from amorphous polymer films