Hydration mechanism of calcium sulfoaluminate-activated supersulfated cement
Zhengning Sun,Song Nie,Jian Zhou,Hui Li,Zhifeng Chen,Mingfeng Xu,Ru Mu,Ying Wang
DOI: https://doi.org/10.1016/j.jclepro.2021.130094
IF: 11.1
2022-01-01
Journal of Cleaner Production
Abstract:Innovations in the cement industry strive towards achieving an eco-friendly alternative to traditional cement. A low-carbon cement, calcium sulfoaluminate-activated supersulfated cement (CSA-SSC), has been recently developed. This cement consists of 80% granulated blastfurnace slag (GBFS), 15% anhydrite, and 5% high-belite calcium sulfoaluminate cement (HB-CSA) clinker. The hydration mechanism of CSA-SSC was experimentally investigated using isothermal calorimetry, X-ray diffraction, thermogravimetric analysis, and scanning electron microscopy, and was numerically studied using thermodynamic modeling. CSA-SSC shows a moderate compressive strength at the early stage, which is mainly attributed to the rapid formation of ettringite from the hydration of C4A3 S ¯ with CaSO4 in HB-CSA clinker. Meanwhile, the hydration of f-CaO in HB-CSA clinker supplies an alkaline environment for the dissolution of GBFS and the formation of more ettringite. In the late stage, apart from ettringite, the hydration of GBFS forms C–S–H, leading to the continuous increase in late strength. A statistical analysis reveals that the high volume of GBFS in CSA-SSC results in a very low direct CO2 emission, which is only 8.7% of that of Portland cement.
environmental sciences,green & sustainable science & technology,engineering, environmental