Abstract:A solid reactive organophosphorus‐nitrogen flame retardant 4N‐BDP was devised and synthesized in order to address the flaws of the widely used organophosphorus flame retardants BDP as well as the issue of flame retardant modification of epoxy resin (EP). A series of flame‐retardant EP composites were prepared by adding 4N‐BDP and BDP to EP in a specific proportion. The flame‐retardant properties of the two were compared, and the flame‐retardant mechanism of 4N‐BDP was deeply analyzed. The results of the UL‐94 test revealed that sample 4N‐BDP‐6 obtained the greatest V‐0 level, while BDP‐6 had no level, when the addition ratio of flame retardant was 8.03%. In the cone calorimeter test, the peak smoke production rate (pSPR) and total smoke production (TSP) of BDP‐6 were not significantly different from those of pure EP. In contrast, TSP and pSPR of 4N‐BDP‐6 decreased by 39.50% and 50.00% respectively compared with EP. Compared with BDP, 4N‐BDP shows better flame retardancy and smoke suppression performance, which can significantly improve the fire resistance of EP. The flame‐retardant mechanism of 4N‐BDP was resolved by scanning electron microscopy, XPS, and thermogravimetric analysis/infrared spectrometry. 4N‐BDP can increase the residual carbon rate of the composites, improve the residual carbon strength, play an excellent condensed phase flame retardant effect, and avoid further decomposition of the materials. In the gas phase, the decomposition of 4N‐BDP produces PO·, PO2· and NH3, which play a good quenching effect and dilution effect. The escape of NH3 will leave bubbles in the residual carbon, making the residual carbon more fluffy, further improving the ability of heat insulation and oxygen insulation, and enhancing the flame retardant effect of the condensed phase. In general, the flame‐retardant mechanism of 4N‐BDP is a synergistic combination of condensed phase and gas phase flame retardant mechanism. This work provides a new approach to improve the defects of organophosphorus flame retardant BDP commonly used in the market and enhance the fire resistance of EP.

Synthesis and flame retardant properties of cyclophosphazene derivatives containing boron

Facile synthesis of a P/N-containing heterocyclic compound for simultaneous enhancement of heat resistance, mechanical properties and fire safety of epoxy resin

Synthesis of a Cyclophosphazene Derivative Containing Multiple Cyano Groups for Electron-Beam Irradiated Flame-Retardant Materials

Synergistic Flame Retardant Effect of an Intumescent Flame Retardant Containing Boron and Magnesium Hydroxide

Synthesis of DOPO-based Cyclotriphosphazene Macromolecule Flame Retardant and Its Performance in Flame-etarded Epoxy Resin

Flame‐retardant Performance and Mechanism of Epoxy Thermosets Modified with a Novel Reactive Flame Retardant Containing Phosphorus, Nitrogen, and Sulfur

Phosphorus‐containing benzoxazine modified epoxy resin: High flame retardancy, low dielectric, and low water absorption

Study on novel boron-containing triazine flame retarded thermoplastic polyester elastomer composites and the flame retardant mechanism

Phosphorus-containing epoxy for flame retardant. I. Synthesis, thermal, and flame-retardant properties

Synthesis and properties of a novel phosphorous-containing flame-retardant hardener for epoxy resin

Synthesis of solid reactive organophosphorus‐nitrogen flame retardant and its application in epoxy resin

Synthesis of decorated polyborosiloxane for enhancing the flame retardancy and mechanical property of epoxy resin

Phosphorous‐nitrogen‐boron decorated graphene hybrid for flame retardancy enhancement of epoxy resin

Facile Synthesis of A Highly Efficient, Halogen-Free, and Intumescent Flame Retardant for Epoxy Resins: Thermal Properties, Combustion Behaviors, and Flame-Retardant Mechanisms

Effect of Borates on Thermal Degradation and Flame Retardancy of Epoxy Resins Using Polyhedral Oligomeric Silsesquioxane As a Curing Agent

Phosphorus-nitrogen synergistic flame retardant (PNFR) towards epoxy resin with excellent flame retardancy and satisfactory mechanical strength: An insight into pyrolysis and flame retardant mechanism

A P/N‐containing flame retardant constructed by phosphaphenanthrene, phosphonate, and triazole and its flame retardant mechanism in reducing fire hazards of epoxy resin

A Phosphorus/nitrogen/boron Co-Curing Agent for Enhancing Flame Retardancy, Mechanical Properties Transparency of Epoxy Resin

Combustion Behavior and Thermal Degradation Properties of Epoxy Resins with a Curing Agent Containing a Caged Bicyclic Phosphate

Synthesis and Properties of a Novel Flame-Retardant Epoxy Resin Containing Biphenylyl/Phenyl Phosphonic Moieties

Synthesis of a novel boron‐containing hyperbranched benzoxazine and its flame‐retardant properties in copolymer with epoxy resin