A Robust Strategy for Crafting Monodisperse Li4Ti5O12 Nanospheres As Superior Rate Anode for Lithium Ion Batteries
Chao Wang,Shuan Wang,Linkai Tang,Yan-Bing He,Lin Gan,Jia Li,Hongda Du,Baohua Li,Zhiqun Lin,Feiyu Kang
DOI: https://doi.org/10.1016/j.nanoen.2016.01.005
IF: 17.6
2016-01-01
Nano Energy
Abstract:The ability to synthesizing monodisperse Li4Ti5O12 (LTO) nanospheres is the key to reducing the irreversible capacity of LTO materials, and thus improving their power performance. However, it remains a grand challenge to achieve uniform precursors of LTO nanospheres and maintain their spherical structures after annealing. Herein, we develop a robust strategy for the synthesis of monodisperse LTO nanospheres with an average diameter of 120nm via the use of titanium nitride (TiN) as a titanium source for lithium ion batteries (LIBs). The precursors composed of uniform TiO2/Li+ nanospheres were formed in a stable alkaline environment during the course of heating of the solution of peroxo-titanium complex as a result of the dissolution of TiN, while TiO2/Li+ microspheres were easily yielded with the decrease in pH value of the precursor solution. The OH− anion was found to effectively retard the hydrolysis of peroxo-titanium complex as well as the aggregation of TiO2/Li+ nanoparticles. Intriguingly, a uniform polyvinyl pyrrolidone (PVP) layer formed in-situ on the surface of TiO2/Li+ nanospheres rendered LTO to retain the monodisperse spherical morphology after annealing. Notably, the as-prepared monodisperse LTO nanospheres comprised of the interconnected LTO nanograins with an average size of ~15nm uniformly coated by a carbon layer derived from the carbonization of PVP exhibited a high tap density (1.1gcm−3) and an outstanding rate-cycling capability. The charge specific capacities at 1, 10, 50 and 80C were 159.5, 151.1, 128.8 and 108.9mAh g−1, respectively. More importantly, the capacity retention after 500 cycles at 10C was as high as 92.6%. This work opens up an avenue to craft the uniform precursors of LTO and thus monodisperse LTO nanospheres that possess superior rate performance with high volumetric energy densities and long-term cyclic stability.