Metal–Organic Framework-Derived Nanoconfinements of CoF 2 and Mixed-Conducting Wiring for High-Performance Metal Fluoride-Lithium Battery
Feixiang Wu,Vesna Srot,Shuangqiang Chen,Mingyu Zhang,Peter A. van Aken,Yong Wang,Joachim Maier,Yan Yu
DOI: https://doi.org/10.1021/acsnano.0c08918
IF: 17.1
2020-12-24
ACS Nano
Abstract:Metal fluoride (MF) conversion cathodes theoretically show higher gravimetric and volumetric capacities than Ni- or Co-based intercalation oxide cathodes, which makes metal fluoride–lithium batteries promising candidates for next-generation high-energy-density batteries. However, their high-energy characteristics are clouded by low-capacity utilization, large voltage hysteresis, and poor cycling stability of transition MF cathodes. A variety of reasons is responsible for this: poor reaction kinetics, low conductivities, unstable MF/electrolyte interfaces and dissolution of active species upon cycling. Herein, we combine the synthesis of the metal–organic-framework (MOF) with the low-temperature fluorination to prepare MOF-shaped CoF<sub>2</sub>@C nanocomposites that exhibit confinement of the CoF<sub>2</sub> nanoparticles and efficient mixed-conducting wiring in the produced architecture. The ultrasmall CoF<sub>2</sub> nanoparticles (5–20 nm on average) are uniformly covered by graphitic carbon walls and embedded in the porous carbon framework. Within the CoF<sub>2</sub>@C nanocomposite, the cross-linked carbon wall and interconnected nanopores serve as electron- and ion-conducting pathways, respectively, enabling a highly reversible conversion reaction of CoF<sub>2</sub>. As a result, the produced CoF<sub>2</sub>@C composite cathodes successfully restrain the above-mentioned challenges and demonstrate high-capacity utilization of ∼500 mAh g<sup>–1</sup> at 0.2C, good rate capability (up to 2C), and long-term cycle stability over 400 cycles. Overall, the presented study not only reports on a simple composite design to achieve high-energy characteristics in CoF<sub>2</sub>–Li batteries but also may provide a general solution for many other metal fluoride–lithium batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c08918?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c08918</a>.HAADF-STEM image of nanocomposite; The XRD patterns of CoF<sub>2</sub>@C in ambient condition and CoF<sub>2</sub>@C under the protection of Kapton; HRTEM images of CoF<sub>2</sub>@C nanocomposite; Raman spectra of the produced and CoF<sub>2</sub>@C nanocomposites; The wetting state of a liquid droplet on the produced CoF<sub>2</sub>@C cathodes; XRD patterns of the CoF<sub>2</sub>@C composite before and after acid washing; discharge–charge voltage profiles and cycle performance of the produced MOF-shaped carbon matrix (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c08918/suppl_file/nn0c08918_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology