Abstract:Yellowish-orange-emitting ZnGeN2 and orange-red-emitting ZnGeN2:Mn were synthesized by a facile and mild gas-reduction–nitridation reaction at 1153K under NH3 flow with air-stable raw materials ZnO, GeO2 and MnCO3. The structure, composition, morphology, photoluminescence and cathodoluminescence properties of ZnGeN2 doped with or without Mn2+ were systematically investigated. Rietveld refinements show that the as-synthesized samples are obtained as single-phase compounds and crystallize as an orthorhombic structure with a space group of Pna21. The actual chemical composition of the as-prepared ZnGeN2 determined by energy dispersive X-ray spectroscopy suggests that the Ge vacancy defects probably exist in the host. The SEM image reveals that the Zn0.99Mn0.01GeN2 particles form aggregates ∼500–600nm in size. The diffuse reflection spectrum and photoluminescence excitation spectrum confirm that the band edge absorption of ZnGeN2 at low energy is 3.3eV (∼376nm). Upon UV light excitation and electron beam excitation, ZnGeN2 gives an intense yellowish-orange emission around 580–600nm, associated with a deep defect level due to the Ge vacancy defects, and ZnGeN2:Mn shows an intense red emission at 610nm due to the 4T1g(4G)→6A1g(6S) of Mn2+. The unusual red emission of Mn2+ in tetrahedral Zn2+ sites is attributed to the strong nephelauxetic effect between Mn2+ and the surrounding tetrahedrally coordinated nitrogen. The photoluminescence and cathodoluminescence emission colors of ZnGeN2:Mn have a high color purity of ∼93–98%. These results demonstrate that ZnGeN2:Mn is a novel, promising red-emitting nitride, potentially applicable to field emission displays with brilliant color-rendering properties and a large color gamut.

Uniform Zinc Germinate Nanostructures: Facile Synthesis, Characterizations, and Luminescence Properties

Controllable Synthesis and Morphology-Dependent Photoluminescence Properties of Well-Defined One-Dimensional Zn2GeO4:Mn2+ Nanostructures

Low-temperature and Short-Time Preparation of Short Rod-Like Zn2GeO4:Mn2+ Luminescent Nanoparticles

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Facile Hydrothermal Synthesis of Mn Doped ZnS Nanocrystals and Luminescence Properties Investigations

Facile Synthesis Of Highly Luminescent Mn-Doped Zns Nanocrystals

Synthesis And Luminescence Of Znmgs : Mn2+ Nanoparticles

Controllable synthesis and morphology-dependent light emission efficiency of Zn 2 GeO 4 nanophosphors

Structure, Composition, Morphology, Photoluminescence and Cathodoluminescence Properties of ZnGeN2 and ZnGeN2:Mn2+ for Field Emission Displays

Controllable Synthesis and Luminescence Properties of Zn2GeO4 : Mn2+ Nanorod Phosphors

Induction of zinc particles on the morphology and photoluminescent property of globular Zn/ZnO core/shell nanorod heterojunction array architectures

Direct Low-Temperature Synthesis of Ultralong Persistent Luminescence Nanobelts Based on a Biphasic Solution-Chemical Reaction

Anomalous Spontaneous-Reduction of Mn7+/Mn4+ to Mn2+ and Luminescence Properties in Zn2geo4:Mn

Photoluminescence and Raman Behaviors of ZnO Nanostructures with Different Morphologies

Rapid growth and photoluminescence properties of doped ZnS one-dimensional nanostructures

Luminescence Property and Synthesis of Sulfur-Doped Zno Nanowires by Electrochemical Deposition

Mn-doped zinc aluminate nanoparticles: hydrothermal synthesis, characterization, and photoluminescence properties.

Modulating emission color in Mn-doped ZnS/ZnO microbelts via thermal evaporation process

Facile Microwave-Assisted Synthesis of Zn2GeO4:Mn2+, Yb3+ Uniform Nanorods and Near-Infrared Down-Conversion Properties

Luminescence properties and the thermal quenching mechanism of Mn 2+ doped Zn 2 GeO 4 long persistent phosphors.

Synthesis And Optoelectrochemical Properties Of Zns:Mn Nanocrystals