Abstract:Silica nanoparticles (nano-silica) were used as synergistic agents with ammonium polyphosphate (APP) and pentaerythritol (PER) to enhance flame retardancy of polypropylene (PP) in this research. The composites were prepared using a melt-mixing method. The influences of nano-silica on the fire performance of composites were thoroughly discussed, which promotes understanding of nano-silica on the flame-retardant performance of polypropylene composite. Scanning electron microscope (SEM) and energy-dispersive spectrometer (EDS) results indicated that the nano-silica with a diameter of about 95 ± 3.9 nm were dispersed favorably in the composite matrix, which might elevate its synergistic effect with intumescent flame retardant and improve the flame retardancy of polypropylene composite. The synergistic effects between nano-silica and intumescent flame retardant on PP composites were studied using the limiting oxygen index (LOI), UL-94 test, and cone calorimeter test (CCT). The total amount of flame retardant was maintained at 30%. When the dosage of nano-silica was 1 wt.%, the LOI value of PP/IFR/Si1.0 composite reached 27.3% and its UL-94 classification reached V-1. Based on the parameters of the CCT, the introduction of nano-silica induced composites with depressed heat release rate (HRR) and peak heat release rate (PHRR). The PHRR of PP/IFR/Si0.5 was only 295.8 kW/m2, which was 17% lower than that of PP/IFR. Moreover, the time to PHRR of PP/IFR/Si0.5 was delayed to 396 s, which was about 36 s later than that without nano-silica. EDS was used to quantitatively analyze the distribution of silica in charred residue. The EDS results indicated that the silica tended to accumulate on the surface during the fire. The surface accumulation characteristic of silica endows it with the enhanced flame-retardant properties of polypropylene composite at a very small dosage (as low as 1 wt.%).

Synergistic Effects of Novel Intumescent Flame Retardant Polypropylene Composites

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

Synergistic effect of porous nickel phosphate VSB-5 on intumescent flame retardant polypropylene composites

Synergistic Effect of Nano-Silica and Intumescent Flame Retardant on the Fire Reaction Properties of Polypropylene Composites.

Synergistic Effects of Nanoporous Nickel Phosphates VSB-1 on Intumescent Flame Retardant Polypropylene Composites

Study on a Novel and Efficient Flame Retardant Synergist–nanoporous Nickel Phosphates VSB‐1 with Intumescent Flame Retardants in Polypropylene

Synergistic Effects of Nano-Bawo4 on Intumescent Flame-Retarded Polypropylene

Synergistic Effect of Novel Synergists–Transition Metal Ion-incorporated Nickel Phosphates with Intumescent Flame Retardants in Polypropylene

Synergistic Effect of Compound Oxides with Intumescent Flame Retardant on the Properties of Polypropylene Composites

Synergistic Effects of Nano-Mn0.4zn0.6fe2o4 on Intumescent Flame-Retarded Polypropylene

Synergistic effect of cocondensed nanosilica in intumescent flame-retardant polypropylene

Synergistic Effect of Phosphorus‐containing Nanosponges on Intumescent Flame‐retardant Polypropylene

Synergistic Effect of SiO2 on Intumescent Flame-retardant Polypropylene

Synergistic Effects of Intumescent Flame Retardant and Nano-Caco3 on Foamability and Flame-Retardant Property of Polypropylene Composites Foams

Synergistic Effect of Zeolite and Hindered Amine Containing Substances on Intumescent Flame Retardant Polypropylene

Synergistic Effect of SiO<sub>2</sub> on Intumescent Flame-retardant Polypropylene

Synergistic Flame Retardant Properties of Polyoxymethylene with Surface Modified Intumescent Flame Retardant and Calcium Carbonate

Flammability of Intumescent Flame-Retarded Nanocomposites of Polypropylene

Synergistic Effect Between Carbon Nanoparticle and Intumescent Flame Retardant on Flammability and Smoke Suppression of Copolymer Thermoplastic Polyurethane

Synergistic effect of nano silicon and piperazine pyrophosphate/melamine polyphosphate on flame retardancy of polypropylene

Synergistic Effects of Ni2+-Fe3+ Layered Double Hydroxide on Intumescent Flame-Retarded Polypropylene Composites Containing Melamine Phosphate and Pentaerythritol Phosphate