Abstract:Sn-doped BiOCl (Sn/BiOCl) photocatalysts were synthesized by a precipitation method using Bi(NO3)(3) center dot 5H(2)O as a bismuth source, SnCl2 as an Sn source, imidazole hydrochloride as a chlorine source, a solvent, and a template agent. The photocatalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy, surface area analysis (Brunauer, Emmett and Teller [BET]), and diffuse reflectance spectroscopy. The XRD results showed a greater increase in the peak intensity of Sn/BiOCl because of its high degree of crystallinity. The UV-Vis results indicated a redshift from 368 nm (BiOCl) to 418 nm (Sn/BiOCl), leading to the reduced band gap of BiOCl because of Sn doping in BiOCl. The Sn/BiOCl not only retained ultraviolet photocatalytic activity of BiOCl but also showed visible photocatalytic activity. The BET results showed that the surface area of Sn/BiOCl (23.35 m(2) ) was bigger than that of BiOCl (13.54 m(2) g). The bigger surface show higher photocatalytic activity due to more contact opportunity between reactants. Hence, the increased photocatalytic activity of Sn/BiOCl in the degradation of rhodamine B can be attributed to a higher degree of crystallinity, larger surface area, and broader range of optical absorption. The Sn/BiOCl needed only 20 min under visible light and 40 min under ultraviolet light to completely degrade rhodamine B. Moreover, the photocatalytic experiment did not require any other chemical reagent such as H2O2. The microstructures of BiOCl and Sn/BiOCl ensured that the catalyst still has high recovery rate when it is reused. The microstructures of catalyst have a little of loss.

Preparation of Bismuth Phosphate Photocatalyst with High Dispersion by Refluxing Method

Room-temperature Fabrication of Bismuth Oxybromide/oxyiodide Photocatalyst and Efficient Degradation of Phenolic Pollutants under Visible Light.

Reflux Preparation and Photocatalytic Performance of Bismuth Phosphate Nanorods

Tuning the Physicochemical Property of BiOBr Via Ph Adjustment: Towards an Efficient Photocatalyst for Degradation of Bisphenol A

Controllable Synthesis and Photocatalytic Performance of Bismuth Phosphate Nanorods

Controlled Synthesis of a Highly Dispersed BiPO4 Photocatalyst with Surface Oxygen Vacancies.

Photodegradation under UV Light Irradiation of Various Types and Systems of Organic Pollutants in the Presence of a Performant BiPO4 Photocatalyst

Preparation and effects of calcining temperature and pH on the photocatalytic activity of BiVO4 microcrystal for degrading methylene blue

Preparation, Performance and Mechanism Study of High-Efficient BiOI/BiOBr Visible Light Photocatalyst

Effects of Distortion of PO4 Tetrahedron on the Photocatalytic Performances of BiPO4

Monoclinic BiPO4: Preparation, photocatalytic properties in experiment and theoretical calculation

Size-Controlled Synthesis Of Bipo4 Nanocrystals For Enhanced Photocatalytic Performance

Facile Preparation of Sn/BiOCl Composite Oxides and Their Photocatalytic Performance

Modification of porous bismuth molybdate for highly removal of antibiotics and H2O2 production

Preparation of Porous Ellipsoidal Bismuth Oxyhalide Microspheres and Their Photocatalytic Performances

Preparation of Bi3.64Mo0.36O6.55 by reflux method and its application in photodegradation of organic pollution

Controlled Synthesis of Bismuth Oxyiodide Toward Optimization of Photocatalytic Performance

Preparation and photocatalytic properties of Ag/BiVO4/BiPO4 heterojunction nanofibers

Zn-ion doped BiOBr for enhanced photocatalytic degradation of methyl blue

Ultrasonic synthesis of controllable thin sheet-like BiPO4 assisted by ionic liquid and Bi-MOF with enhanced visible-light photocatalytic activity

Synthesis, Crystal Structure, Photodegradation Kinetics and Photocatalytic Activity of Novel Photocatalyst ZnBiYO4