Enhanced Thermoelectric Properties in Ge-doped and Single-Filled Skutterudites Prepared by Unique Melt-Spinning Method

Nusrat Shaheen,Muhammad Sufyan Javed,Hidayat Ullah Shan,Shahid Hussain,Muhammad Ashfaq Ahmad,Rizwan Raza,Muhammad Saleem,Xiaoyuan Zhou
DOI: https://doi.org/10.1016/j.ceramint.2018.04.058
IF: 5.532
2018-01-01
Ceramics International
Abstract:In this paper, we determined an effective substitution of Ge at Sb sites in Nd-filled p-type skutterudites, a series of Nd.9Fe2Co2Sb12-xGex compounds with compositions of x = 0, 0.1, 0.2, 0.3 and 0.4 were synthesized by homemade induction melting, assembled inside the glove box and followed by spark plasma sintering process (SPS). The thermoelectric properties are investigated as a function of Ge doping content with fixed Nd-filler at 0.9 and the formation of skutterudite phase is characterized by X-ray diffraction. All samples possess positive Seebeck coefficients, representing effective p-type doping. It is observed that the electrical conductivity decreases with decreasing Ge doping concentrations while increased with temperature due to bipolar effect. The lightly doped samples (x = 0.1 and 0.2) have lower lattice thermal conductivity over the entire temperature range, in which x = 0.2 sample shows the highest ZT value of 0.82 at 700 K, which is 30% higher than that of the Ge-free sample. The improvement in ZT can be attributed to the optimized carrier concentration and reduced thermal conductivity. The enhancement of ZT through Ge doping, coupled with drastically reduced processing time, shows that these compounds may have great potential in application as p-type segments of the thermoelectric devices.
What problem does this paper attempt to address?