Six New Members of the A(2)M(II)M(3)(IV)Q(8) Family and Their Structural Relationship

Xiao-Ning Hu,Lin Xiong,Li-Ming Wu

DOI: https://doi.org/10.1021/acs.cgd.8b00247

IF: 4.01

2018-01-01

Crystal Growth & Design

Abstract:The A(2)M(II)M(3)(IV)Q(8) family (A = alkali metal; M-II = divalent metal; M-IV = tetravalent metal; Q= chalcogenide) has attracted much attention because of its diverse structures and properties. Herein, we have successfully synthesized six new compounds as the first Mn-containing members of this family, Cs2MnGe3S8 (1), Cs2MnGe3Se8 (2), Cs2MnSn3Se8 (3), Rb2MnGe3S8 (4), Rb2MnGe3 Se-8 (5), and Rb2MnSn3Se8 (6). Compounds 1 and 6 crystallize in the monoclinic space group P2(1)/n (No. 14) and P2(1) (No. 4), respectively, whereas compounds 2-5 crystallize in the non-centrosymmetric orthorhombic P2(1)2(1)2(1) (No. 19). According to our theoretical calculations, their energy gaps are mainly dominated by s states of M-IV and p states of Q and minor Mn 3d. Plate-like crystals with sizes about 20 X 5 X 1 mm(3) of 2 and 3 are obtained by the Bridgeman method. In addition, we propose a structure mismatch factor that is defined as F = r(M)(II)+ r(M)(IV) + 2r(Q)(2-) - 2r(A)+ to provide a clear description of how three different structure types distribute among the A(2)M(II)M(3)(IV)Q(8) family; when 1.2 < F < 1.9, members will adopt a P2(1)2(1)2(1)-type structure; when F is too small (<1.2) or too large (>1.9), P2(1)/n or P2(1)-type, respectively, will be taken.