Abstract:Purpose In summary, it can be found that the current research on the simulation of natural atmospheric dry–wet alternating accelerated corrosion mainly focused on the study of electrochemical corrosion process and the study of corrosion rate; the micro-pre-corrosion mechanism of materials in this environment, especially for materials. The specific effects of fatigue and fracture performance still lack detailed research. Accordingly, this study aims to more realistically simulate the effect of natural atmospheric corrosion environment on the corrosion resistance and fatigue performance of aircraft skin. Design/methodology/approach In this study, the uniaxial strain control method was used to test the fatigue performance of pre-corrosion samples under simulated natural atmospheric corrosion using MTS809 tensile-torque composite fatigue machine. Scanning electron microscopy, X-ray energy spectrum analysis, atomic force microscopy and X-ray diffraction analysis were used. Fatigue fracture, corrosion morphology and corrosion products were analyzed. Findings The results show that the deep corrosion pit caused by pre-corrosion environment leads to multi-source initiation of crack; the fatigue life of pre-corroded sample decreases by about one-half, chloride ion invades the material and promotes intergranular corrosion; life prediction results show that the natural atmospheric corrosive environment mainly affects the plastic term in the Manson–Coffin formula resulting in a decrease in fatigue life. Originality/value Innovative experimental schemes and materials are used and the test temperature and relative humidity are strictly controlled. The corrosion failure mechanism of 2A70-T6 aluminum alloy under alternating wet and dry accelerated corrosion environment and its influence on fatigue behavior were obtained.

Uniaxial Low Cycle Fatigue Behavior for Pre-Corroded 16MND5 Bainitic Steel in Simulated Pressurized Water Reactor Environment

Corrosion Behavior of 16mnr Steel and Welded Joints in High-Temperature Naphthenic Acid

Low Cycle Fatigue Behavior and Failure Mechanism of Wire Arc Additive Manufacturing 16MND5 Bainitic Steel

Corrosion Fatigue Behavior of 316LN Stainless Steel Hollow Specimen in High-Temperature Pressurized Water

Creep-fatigue Properties and Deformation Mechanism of 316L Steel Fabricated by Laser Powder Bed Fusion (PBF-LB/M)

Effect of Repeated Weld Repairs on Microstructure and Mechanical Properties of Heat-Affected Zone in CA6NM Stainless Steel

Experimental Study on Fatigue Crack Growth and Residual Strength of Steel 30crmnsini2a under Mixed Corrosive Environments

Environmental Fatigue Crack Propagation Behavior of Cast Stainless Steels under PWR Condition

Effects of pressurized water reactor environment and cyclic loading parameters on the low cycle fatigue behavior of 304L stainless steel

Low-cycle Fatigue Behavior and Corrosion Mechanism of Pre-Corroded 2A70-T6 Aluminum Alloy

Fatigue Behavior of 316 L Stainless Steel Weldment Up to Very-High–cycle Fatigue Regime

Fatigue Crack Initiation Behaviors of Nuclear Power Plant Main Pipe Stainless Steel in Water with High Temperature and High Pressure

Differences of Corrosion Fatigue Behaviors among 316LN Base Metal, 316LN Heat-Affected Zone and 308L Weld Metal in a Safe-End Weld Joint in Borated and Lithiated High-Temperature Water

Experimental and Numerical Investigation on Mechanical and Fatigue Performance of Corroded Q690D High-Strength Steel

CORROSION FATIGUE OF NUCLEAR-GRADE STAIN- LESS STEEL IN HIGH TEMPERATURE WATER AND ITS ENVIRONMENTAL FATIGUE DESIGN MODEL

Microstructural Evolution and Oxidation Behaviour of CF8A Austenitic Stainless Steel During Corrosion Fatigue in a Simulated Pressurised Water Reactor Environment

Effect of Sulfur and Dissolved Oxygen Content on Corrosion Fatigue Property in High Temperature and High Pressure Water

The microstructure and tensile fracture behavior of long term thermal aged Z3CN20-09M stainless steel

Improvement of Stress Corrosion Cracking Resistance by Low Cycle Fatigue of a CrNiMoV Steel

Stress Corrosion Cracking and Mechanical Behaviors of Domestic Low Alloy Steel SA-508III in Simulated PWR Primary Water Environment

LOW CYCLE FATIGUE BEHAVIOR OF PWR PRIMARY PIPE MATERIAL FOR NUCLEAR POWER PLANT