The Dual-Model Up/Down-Conversion Green Luminescence of Gd6o5f8:Yb3+,Ho3+,Li+ and Its Application for Temperature Sensing
Shanshan Du,Deyin Wang,Qinping Qiang,Xinlong Ma,Zuobin Tang,Yuhua Wang
DOI: https://doi.org/10.1039/c6tc01812b
IF: 6.4
2016-01-01
Journal of Materials Chemistry C
Abstract:Micro-sized Gd6O5F8 particles doped with Yb3+, Ho3+ and Li+ ions have been synthesized by a facile hydrothermal route. The dual-model up- and down-conversion luminescence was investigated under visible blue (VIS-B) light (451 nm) and near infrared (NIR) light (980 nm) excitations. The structural properties of the products are analysed by X-ray diffraction (XRD). Upon excitation to the F-2(5/2) level of Yb3+ using a 980 nm laser diode, Gd6O5F8:Yb3+,Ho3+ exhibits intense up-converted green and red emission at 545 nm and 660 nm, which correspond to the S-5(2) -> I-5(8) and F-5(5) -> I-5(8) transitions of Ho3+, respectively. The nearly quadratic dependence of the green/red emission intensity on the excitation power indicates that a two-photon up-conversion process was involved to populate the green (S-5(2)) and red levels (F-5(5)) of Ho3+. In contrast, upon excitation Ho3+ to its F-5(1) level by 451 nm blue light, both visible and near-infrared emissions peaking at 545 nm, 660 nm, 980 nm and 1191 nm are simultaneously observed in the emission spectra, which are assigned to the S-5(2) -> I-5(8) (Ho3+), F-5(5) -> I-5(8) (Ho3+), F-2(5/2) F-2(7/2) (Yb3+) and I-5(6) -> I-5(8) (Ho3+) transitions, respectively. Meanwhile, the emission intensities of the up-converted green emission and down-converted emissions were further enhanced by co-doping Li+ which can be confirmed by the fact that the emission intensities of the up-converted green emission and down-converted NIR emission were increased 50% and 90% after co-doping 7% L+ The energy transfer processes between Ho3+ and Yb3+ ions and the mechanisms of Li+ doping for the emission enhancement have been investigated and discussed. Additionally, the time-resolved luminescence traces are measured, and the luminescence lifetimes of the Ho3+ ions are calculated. Furthermore, the temperature-dependent up-conversion and down-shifted luminescence of Gd6O5F8:Yb3+,Ho3+,Li+ are investigated, and the results show that the ratio of up-converted green to red emission as well as the ratio of down-shifted green to blue emission in Gd6O5F8:Yb3+,Ho3+,Li+ all respond single exponentially to temperature, which could be applied to sense temperature.