Strong, Ultrafast, Reprogrammable Hydrogel Actuators with Muscle-Mimetic Aligned Fibrous Structures
Zhen Jiang,Seyed Mohsen Seraji,Xiao Tan,Xinxing Zhang,Toan Dinh,Mahdie Mollazade,Alan E. Rowan,Andrew K. Whittaker,Pingan Song,Hao Wang
DOI: https://doi.org/10.1021/acs.chemmater.1c02312
IF: 10.508
2021-09-23
Chemistry of Materials
Abstract:Hydrogel actuators displaying programmable shape transformations promise to be core components in future biomedical and soft robotic devices. However, current hydrogel actuators have shortcomings, including poor mechanical properties, slow response, and lack of shape reprogrammability, which limit their practical applications . Existing molecular designs offer limited efficiency in synergistically addressing these issues in a single hydrogel system. Herein, we propose a strategy to develop hydrogel actuators with muscle-mimetic aligned microfibrillar morphology, combining thermoinduced microphase separation and mechanical alignment. The key to our design is the introduction of metal–phenolic complexes, which not only induce irreversible sol–gel transition via the concentrated coordinate ions above lower critical solution temperature (LCST) but also fix the alignment of bundle network due to dynamic network rearrangement. Our design concept is observed to simultaneously achieve excellent mechanical properties (tensile strength ≈ 1.27 MPa, toughness ≈ 2.0 MJ m–3) and ultrafast actuation (40.1% thermal contraction as short as 1 s), which is a long-lasting challenge in the field. In addition, the dynamic hydrogels can be reprogrammed into spiral, helical, and biomimetic actuators. This work opens new opportunities to realize real-world applications for smart hydrogels as soft machines by fundamentally breaking the current property limit.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c02312.Synthetic route for poly(MAA-co-OEGMA); FTIR spectra, intensity size distribution, UV/vis spectra, and DSC curve and storage modulus and loss modulus as a function of frequency for poly(MAA-co-OEGMA)/TA/Fe3+ aqueous solution and the thermogel; ζ-potentials for tannic acid and poly(MAA-co-OEGMA)/TA/Fe3+ aqueous solution; photographs for heating and cooling of poly(MAA-co-OEGMA)/Fe3+ aqueous solution; photographs, SEM image, and stress relaxation for thermogels; and tensile strain–stress curves, SEM images, and photographs of shape transformations for aligned thermogels (PDF)Shape transformation of isotropic bulk hydrogel at the hot water of 50 °C (MP4)Thermal contraction of anisotropic hydrogel at the hot water of 50 °C (MP4)Recovery of thermocontracted anisotropic hydrogel at the cool water of 25 °C (MP4)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical