Abstract:To afford an intact double network (sample abbr.: DN) hydrogel, two-step crosslinking reactions of poly(2-acrylamido-2-methylpropanesulfonic acid) (i.e., PAMPS first network) and then poly(acrylic acid) (i.e., PAA second network) were conducted both in the presence of crosslinker (N,N′-methylenebisacrylamide (MBAA)). Similar to the two-step processes, different contents of 2,2,6,6-tetramethyl-1-piperidinyloxy (TEMPO) oxidized cellulose nanofibers (TOCN: 1, 2, and 3 wt.%) were initially dispersed in the first network solutions and then crosslinked. The TOCN-containing PAMPS first networks subsequently soaked in AA and crosslinker and conducted the second network crosslinking reactions (TOCN was then abbreviated as T for DN samples). As the third step, various (T–)DN hydrogels were then treated with different concentrations of FeCl3(aq) solutions (5, 50, 100, and 200 mM). Through incorporations of ferric ions into (T–)DN hydrogels, notably, three purposes are targeted: (i) strengthen the (T–)DN hydrogels through ionic bonding, (ii) significantly render ionic conductivity of hydrogels, and (iii) serve as a catalyst for the forth step to proceed with in situ chemical oxidative polymerizations of pyrroles to afford polypyrrole-containing (sample abbr.: Py) hydrogels [i.e., (T–)Py–DN samples]. The characteristic functional groups of PAMPS, PAA, and Py were confirmed by FT–IR. Uniform microstructures were observed by cryo scanning electron microscopy (cryo-SEM). These results indicated that homogeneous composites of T–Py–DN hydrogels were obtained through the four-step process. All dry samples showed similar thermal degradation behaviors from the thermogravimetric analysis (TGA). The T2–Py5–DN sample (i.e., containing 2 wt.% TOCN with 5 mM FeCl3(aq) treatment) showed the best tensile strength and strain at breaking properties (i.e., σTb = 450 kPa and εTb = 106%). With the same compositions, a high conductivity of 3.34 × 10−3 S/cm was acquired. The tough T2–Py5–DN hydrogel displayed good conductive reversibility during several “stretching-and-releasing” cycles of 50–100–0%, demonstrating a promising candidate for bioelectronic or biomaterial applications.

Tuning morphology and mechanical property of polyacrylamide/Laponite/titania dual nanocomposite hydrogels by titania

Stretchable Dual Nanocomposite Hydrogels Strengthened by Physical Interaction Between Inorganic Hybrid Crosslinker and Polymers

Mechanically Robust Polyacrylamide Composite Hydrogel Achieved by Integrating Lamellar Montmorillonite and Chitosan Microcrystalline Structure into Covalently Cross-linked Network

Multi-physically Cross-Linked Hydrogels Simultaneously with MPa Level Mechanical Strengths and High Equilibrium Water Content above 70 %

Tough Supramolecular Hydrogels with Excellent Self-Recovery Behavior Mediated by Metal-Coordination Interaction

Strengthening Network of Polyacrylic Acid/Silica Nanocomposite Hydrogels

Preparation and Properties of Polyacrylamide/ Titanium Oxide Hydrogels

Strong and Tough Polyacrylamide/laponite Nanocomposite Hydrogels Modified with 1-Butyl-3-methylimidazolium Chloride Salt

Structure Optimization and Mechanical Model for Microgel-Reinforced Hydrogels with High Strength and Toughness

Dual Ionically Cross-linked Double-Network Hydrogels with High Strength, Toughness, Swelling Resistance, and Improved 3D Printing Processability

Thermoresponsive nanocomposite hydrogels with high mechanical strength and toughness based on a dual crosslinking strategy

Studies on the Properties and Formation Mechanism of Flexible Nanocomposite Hydrogels from Cellulose Nanocrystals and Poly(Acrylic Acid)

Strengthening mechanism of poly(acrylamide)/graphene oxide/laponite dual nanocomposite hydrogels

Ratiometric fluorescent probe based on gold nanoclusters and alizarin red-boronic acid for monitoring glucose in brain microdialysate.

Phase Transition Temperature Controllable Poly(acrylamide- Co -Acrylic Acid) Nanocomposite Physical Hydrogels with High Strength

Super tough bentonite/SiO 2 -based dual nanocomposite hydrogels using silane as both an intercalator and a crosslinker

Multi-responsive nanocomposite hydrogels with high strength and toughness.

Adjusting Some Properties of Poly(methacrylic acid) (Nano)Composite Hydrogels by Means of Silicon-Containing Inorganic Fillers

High strength nanocomposite hydrogels with outstanding UV‐shielding property

The preparation of double network hydrogel with high mechanical properties by photopolymerization under the green LED irradiation and enhancement of wet adhesion by tannic acid

Preparations of Tough and Conductive PAMPS/PAA Double Network Hydrogels Containing Cellulose Nanofibers and Polypyrroles