Abstract:Aramid copolymers have garnered significant interest due to their potential applications in extreme environments such as the aerospace, defense, and automotive industries. Recent developments in aramid copolymers have moved beyond their traditional use in high-strength, high-temperature resistant fibers. There is now a demand for new polymers that can easily be processed into thin films for applications such as electrical insulation films and membranes, utilizing the inherent properties of aramid copolymers. In this work, we demonstrate two novel aramid copolymers that are capable of polymerizing in polar organic solvents with a high degree of polymerization, achieved by incorporating flexible bis(4-aminophenoxy) benzene moieties into the chain backbone. The synthesized MBAB-aramid and PBAB-aramid have enabled the fabrication of exceptionally thin, clear films, with an average molecular weight exceeding 150 kDa and a thickness ranging from 3 to 10 μm. The dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA) reveal that the thin films of MBAB-aramid and PBAB-aramid exhibited glass transition temperatures of 270.1 °C and 292.7 °C, respectively, and thermal decomposition temperatures of 449.6 °C and 465.5 °C, respectively. The mechanical tensile analysis of the 5 μm thick films confirmed that the tensile strengths, with elongation at break, are 107.1 MPa (50.7%) for MBAB-aramid and 113.5 MPa (58.4%) for PBAB-aramid, respectively. The thermal and mechanical properties consistently differ between the two polymers, which is attributed to variations in the linearity of the polymer structures and the resulting differences in the density of intermolecular hydrogen bonding and pi-pi interactions. The resulting high-strength, ultra-thin aramid materials offer numerous potential applications in thin films, membranes, and functional coatings across various industries.

Facile Preparation And Characterization Of Soluble Aramid

Facile synthesis and characterization of soluble aramid containing polar hydroxyl side group

Novel Thermally Stable and Organosoluble Aromatic Polyamides with Main Chain Phenyl-1,3,5-Triazine Moieties

Novel Bis(4-aminophenoxy) Benzene-Based Aramid Copolymers with Enhanced Solution Processability

Facile Polycyclotrimerization of "simple" Arylene Bipropiolates: A Metal-Free, Regioselective Route to Functional Hyperbranched Polymers with High Optical Transparency, Tunable Refractive Index, Low Chromatic Aberration, and Photoresponsive Patternability

Preparation and application of aramid nanofiber via carbodiimide assisted polymerization

Synthesis and Characterization of New Aramids Based on O-(M-triphenyl)-terephthaloyl Chloride and M-(M-triphenyl)-isophthaloyl Chloride

Synthesis and Characterization of Novel Semiaromatic Copolyamides Bearing Both Polar Hydroxyl and Unsaturated Allyl Substituents

Rapid and Scalable Synthesis of Novel Carboxylated Aramid Nanofibers for Simultaneously Improving the Strength and Toughness of Carbon Fiber/epoxy Laminates

Enhancement of Para-Aramid Fibers by Depositing Poly-P-paraphenylene Terephthalamide Oligomer Modified Multi-Walled Carbon Nanotubes

Dispersions of aramid nanofibers: a new nanoscale building block

Facile Polymerization of Water and Triple-Bond Based Monomers Toward Functional Polyamides

Efficient mechanochemically for the preparation of high performance aramid nanofibers and KOH/DMSO superbase

Preparation and Properties of Mechanically Robust, Colorless, and Transparent Aramid Films

A Facile Method to Prepare Nanoscale Polyacrylonitrile Particles Grafted Aramid Fibers for Superior Interfacial and Mechanical Properties of Epoxy Composites

Synthesis and Characterization of Novel Aromatic Polyamides Via Yamazaki-Higashi Phosphorylation Method

Synthesis and Properties of Poly(p-Phenylene Terephthalamide) Bearing Both Polar and Unsaturated Substituents Introduced Via Claisen Rearrangement Reaction

New Soluble Aromatic Polyamides from Non-Symmetrical Extended Diacid Containing A Phthalazinone Moiety

Synthesis of well‐defined aromatic poly(amide‐ether)s via chain‐growth condensation polymerization

Timesaving, High-Efficiency Approaches to Fabricate Aramid Nanofibers

Aromatic Polyamide Brushes for High Young's Modulus Surfaces by Surface-Initiated Chain-Growth Condensation Polymerization