Abstract:Hysteresis related to first-order phase transformation in shape memory alloys, which is the macroscopic manifestation of energy dissipation, is detrimental to the precise control of actuation and causes structural and functional fatigue of components. It is of vital importance to explore high-performance shape memory alloys with low stress-hysteresis, large superelasticity, and wide temperature range operation in practical applications. Here, we have developed a Ni-Mn-Fe-In shape memory microwire, exhibiting an ultra-low stress-hysteresis and huge tensile superelasticity in a wide temperature range. The microwire shows a smooth surface and a single crystal structure (with ⟨001⟩A-oriented along the axial direction of microwire), and the microstructure of the microwire contains austenite matrix and sparsely distributed precipitates with an average size of 20–80 nm, all of which may be beneficial to obtain low hysteresis and large strains in the microwire. As a result, the microwire exhibits a minimum stress-hysteresis of as low as 8.5 MPa (with overall strain of 15.3%) and corresponding energy dissipation as low as 1.44 MJ/m3. The microwire always shows a low stress-hysteresis (less than 24 MPa) and low energy dissipation (less than 2.86 MJ/m3) above room temperature. The microwire shows a huge superelasticity with recoverable strains higher than 15% in the wide temperature range from 218 to 418 K. Together with the advantages of easy fabrication and no post-processing required, this microwire shows a tremendous potential for cyclic actuators and energy conversion devices under multi-field coupling.

Elastocaloric Effects in Ultra-Fine Grained NiTi Microwires Processed by Cold-Drawing

Enhanced Elastocaloric Stability in NiTi Alloys under Shear Stress

Enhanced Cyclic Stability of Elastocaloric Effect in Oligocrystalline Cu–Al–Mn Microwires Via Cold-Drawing

Martensitic transformation and elastocaloric effect of Ti-Ni-Cu-Al microwire

Imparting High Elastocaloric Cooling Potential to NiTi Alloy by Two-Step Enhancements

Elastocaloric Effect Induced by the Rubber-Like Behavior of Nanocrystalline Wires of A Ti-50.8ni (at.%) Alloy

Elastocaloric effects related to B2↔R and B2↔B19′ martensite transformations in nanocrystalline Ni50.5Ti49.5 microwires

Elastocaloric effect with a broad temperature window and low energy loss in a nanograin Ti-44Ni-5Cu-1Al ( at · % ) shape memory alloy

Elastocaloric Effect with Small Hysteresis in Bamboo-Grained Cu–Al–Mn Microwires

Ultra-low stress-hysteresis and huge superelasticity in NiMn-based shape memory microwire

Study of the elastocaloric effect and mechanical behavior for the NiTi shape memory alloys

Ultra-wide-temperature-range superelasticity and intrinsic two-way shape memory effect in Co–Ni–Ga microwires

Energy-Efficient Elastocaloric Cooling by Flexibly and Reversibly Transferring Interface in Magnetic Shape-Memory Alloys

Enhanced superelasticity and reversible elastocaloric effect in nano-grained NiTi alloys with low stress hysteresis

Endowing Low Fatigue for Elastocaloric Effect by Refined Hierarchical Microcomposite in Additive Manufactured NiTiCuCo Alloy

Temperature Dependence of Elastocaloric Effect in a Microstructurally Graded NiTi Alloy

Ultrahigh cycle fatigue of nanocrystalline NiTi tubes for elastocaloric cooling

Achieving stable actuation response and elastocaloric effect in a nanocrystalline Ti50Ni40Cu10 alloy

Microstructures of Ti–Ni–Fe Wire after Severe Cold-Drawing and Annealing

Excellent mechanical properties and giant room-temperature elastocaloric effect in spark plasma sintered Ni-Co-Mn-Ti shape memory alloy

Reversible Elastocaloric Effects with Small Hysteresis in Nanocrystalline Ni-Ti Microwires