Abstract:Graphene research has captivated researchers worldwide, propelling innovation across diverse industries. Through the liquid-phase exfoliation methodology of graphite powder, we have demonstrated a rapid route for obtaining few-layer and multi-layer graphene using a natural surfactant, cardanol. Aqueous phase exfoliation of graphite in the presence of cardanol as a surfactant was conducted to obtain pre-exfoliated graphite suspensions. The influence of different ultrasonication times, 10, 20, and 30 min, and contact times with the surfactant, 1 and 60 min, on the stability and concentration of dispersed exfoliated graphite was evaluated. Results indicate that ultrasonication for 20 min resulted in improved stability and reduced graphene flake sizes, making it suitable for scalable graphene production. Subsequently, the most stable dispersions of exfoliated graphite were subjected to CO 2 -pressurized treatment. Promising results were obtained when employing cardanol at its critical micelle concentration. The graphene exhibited good structural quality, low defect density, and small stacking, with an average size of 15 nm, where 40 % of the stacked graphene was smaller than 5 nm. The findings provide valuable recommendations for the scalable production of graphene with multilayers and a few layers (FLG/MLG), using cardanol, a friendly surfactant, and a novel method of exfoliation utilizing supercritical CO 2 . This technology represents an innovative approach, with potential applications in supercapacitors, solar cells, biosensors, polymer composites, and advanced materials.

Exfoliation of Graphite in CO2 Expanded Organic Solvents Combined with Low Speed Shear Mixing

High-pressure Induced Exfoliation for Regulating the Morphology of Graphene in Supercritical CO2 System

Solvothermal-assisted Exfoliation Process to Produce Graphene with High Yield and High Quality

Insightful Understanding of Shear-Assisted Supercritical CO2 Exfoliation for Fabricating Graphene Nanosheets Through the Combination of Kinetics and Process Parameters

Low-temperature Exfoliation of Multilayer-Graphene Material from FeCl3 and CH3NO2 Co-Intercalated Graphite Compound.

Large-Scale Graphene Production by Ultrasound-Assisted Exfoliation of Natural Graphite in Supercritical Co2/H2o Medium

Effect of Static Pressure on Ultrasonic Liquid Phase Exfoliation of Few-Layer Graphene

Synergistic Effect of Supercritical CO2 and Organic Solvent on Exfoliation of Graphene: Experiment and Atomistic Simulation Studies.

From Graphite to Graphene: Direct Liquid-Phase Exfoliation of Graphite to Produce Single- and Few-Layered Pristine Graphene

Few-layer graphene production through graphite exfoliation in pressurized CO 2 assisted by natural surfactant

Advancement In Liquid Exfoliation Of Graphite Through Simultaneously Oxidizing And Ultrasonicating

Direct Exfoliation of Graphene in Organic Solvents with Addition of NaOH.

Preparation of Graphene by Supercritical CO2 Circulating Exfoliation with a Jet Cavitation

The Production of Graphene Using Impinging Jet Exfoliation in a Binary System of CO2 and N-methyl Pyrrolidone.

Production of Graphene Nanosheets by Supercritical CO2 Process Coupled with Micro-Jet Exfoliation

Efficient Exfoliation of Graphite in Chloroform with a Pyrene-Containing Hyperbranched Polyethylene As Stabilizer to Render Pyrene-Functionalized High-Quality Graphene

High concentration and stable few-layer graphene dispersions prepared by the exfoliation of graphite in different organic solvents

Impact of Ultrasonic Probe Type, Frequency, and Static Pressure on Large-Scale Graphene Exfoliation

Exfoliation and Dispersion of Graphene in Ethanol-Water Mixtures

Liquid-phase Exfoliation of Graphene in Organic Solvents with Addition of Naphthalene.

A Mixed-Solvent Strategy for Facile and Green Preparation of Graphene by Liquid-Phase Exfoliation of Graphite