Abstract:The microstructure, texture and mechanical properties evolution of the extruded fine-grained Mg-(1, 5) Y (wt%) alloy sheets were investigated during annealing. The as-extruded sheets exhibited a fully dynamic recrystallized (DRXed) microstructure consisting of uniform and fine equiaxed grains (5.7-8.7 mu m) and a small amount of YH2 second phase particles. Both sheets exhibited significant thermal stability at 300 degrees C annealing and remarkable grain growth at temperatures higher than 400 degrees C. The measured grain growth activation energy (Q) of Mg-1Y at all temperatures tested was 91 +/- 3 kJ/mol, suggesting that the growth was controlled by grain boundary diffusion. Meanwhile, for Mg-5Y alloy at lower temperatures (300-400 degrees C), the Q value (59 kJ/mol) indicated that the grain growth was controlled by grain boundary diffusion while the Q value (175 kJ/mol) at higher temperatures (400-450 degrees C) implied that lattice self-diffusion controlled the process. A representative rare-earth texture was present for both sheets in the as-extruded condition, and remarkable basal texture weakening was observed with the grain growth during each isothermal annealing process. The texture weakening can be ascribed to the preferential growth of non-basal oriented grains based on the EBSD analysis, which was likely related to the segregation of Y atoms at grain boundaries. The microhardness and grain size relationship can be described well by the Hall-Petch relation for all the annealed sheets, while the yield stress was not the case indicating that the macroscopic strength was more sensitive to the texture than the localized microhardness.

Microstructure, Texture and Mechanical Properties Evolution of Extruded Fine-Grained Mg-Y Sheets During Annealing