Monolithic Crystalline Swelling of Graphite Oxide: A Bridge to Ultralarge Graphene Oxide with High Scalability

Jiajia Zhang,Qiangqiang Liu,Yingbo Ruan,Shan Ling,Ke Wang,Hongbin Lu

DOI: https://doi.org/10.1021/acs.chemmater.7b04458

IF: 10.508

2018-01-01

Chemistry of Materials

Abstract:The large-scale preparation of ultralarge graphene oxide (ULGO) is urgently needed for developing advanced devices and high-performance nanocomposites. However, it is extremely difficult to produce ULGO in an industrially viable, high-efficiency manner due to the inevitable sheet fragmentation and significant gelation behavior occurred in existing methods. We propose a stationary oxidation-monolithic crystalline swelling strategy that can completely convert graphite to ULGO. This new stationary oxidation method minimizes the sheet fracture and prevents the exfoliation of oxidized layers without sacrificing the oxidation rate, resulting in oxidized flakes with high crystalline and lateral sizes the same as raw graphite. The oxidized graphite flakes undergo a monolithic crystalline swelling during the purification, leading to the formation of a three-dimensional order structure without peeling. This enables graphite oxide to be purified by spontaneous sedimentation within 1 hour as gelation is avoided and to be exfoliated exhaustively into single-layered ULGO sheets through mild mechanical shaking, with an average size of 108 mu m and the largest size of 256 mu m. These ULGO sheets can form liquid crystals at a record dispersion concentration (as low as 0.2 mg/mL). The ULGO papers show outstanding mechanical properties and electrical conductivities (after HI reduction) that outperform the reported results.