A 3D porous nitrogen-doped carbon nanotube sponge anode modified with polypyrrole and carboxymethyl cellulose for high-performance microbial fuel cells
Yuyang Wang,Xu Pan,Ye Chen,Qing Wen,Cunguo Lin,Jiyong Zheng,Wei Li,Haitao Xu,Lijuan Qi
DOI: https://doi.org/10.1007/s10800-020-01488-z
IF: 2.925
2020-09-26
Journal of Applied Electrochemistry
Abstract:Enhancing anode performance is a critical step to improving the power output and energy storage of microbial fuel cells (MFCs). In this study, MFCs containing pseudocapacitive anode materials, such as polypyrrole-carboxymethyl cellulose (PPy-CMC) composite films, were used to coat the nitrogen-doped carbon nanotube (N-CNT)/sponge (S) for use in MFCs. The capacitive anode could function as a bioanode, store electrons generated from the microbial oxidation of a substrate, and release the accumulated charge as needed. Scanning electron microscopy results indicated that the composite anode had a three-dimensional macroporous structure with a large specific surface area, providing more sites for microbial attachment and growth. Experimental results showed that MFCs equipped with PPy-CMC/N-CNT/S capacitive bioanodes had a maximum power density of 4.88 W m<sup>−3</sup>, which was 1.34 and 1.71 times as much as those of PPy/N-CNT/S and N-CNT/S bioanodes (3.65 and 2.85 W m<sup>−3</sup>), respectively. Moreover, the charge–discharge time of 60–90 min, the total charge <i>Q</i><sub>m</sub> of the MFC equipped with the PPy-CMC/N-CNT/S anode was the largest (5154.08 mC cm<sup>−2</sup>)—5.7 times higher than that of the N-CNT/S anode. The excellent performance of the MFC equipped with the PPy-CMC/N-CNT/S anode was attributable to the composite materials, which exhibited a large-pore structure, good biocompatibility, large capacitance, and high specific surface area. Therefore, this synthesized composite exhibited potential as a capacitive and biocompatible anode material in MFCs.
electrochemistry