In situ removal of Cr 6+ with an intelligent adsorbent: Microwave synthesis, interface adsorption, thermodynamics, mechanism and self-regeneration
Baoxiu Zhao,Bo Gao,Huanxin Shi,Yiran Xue,Ning Chen,Hao Xu,Yulu Xing,Xuan Zhao,Bingrui Ma,Jie Liu,Jincheng Li
DOI: https://doi.org/10.1016/j.jece.2024.112045
IF: 7.7
2024-02-05
Journal of Environmental Chemical Engineering
Abstract:An intelligent adsorbent for Cr 6+ was prepared with microwave irradiation, using carboxymethyl cellulose (CMC) and acrylamide (AM) as grafted skeleton and monomer . Preparation conditions including microwave power, time, crosslinker, initiator and molar ratio of CMC to AM were all optimized, and characterizations of CMC-AM were performed with XRD, SEM, FTIR, XPS, TG, etc. Adsorption tests such as static and dynamic breakthrough curve were both carried out. 99% Cr 6+ ions were removed by CMC-AM when Cr 6+ concentration was 1.5 mg·L -1 , pH value was 5 and CMC-AM dosage of was 1.0 g·L -1 . The adsorption kinetics fitted well with pseudo-second order reaction and adsorption equilibrium accorded well with Langmuir isothermal model. It was observed that adsorption of Cr 6+ was a spontaneous endothermic reaction based on values of ∆G, ∆S and ∆H. According to XPS analysis, it was found that Cr 3+ appeared on the surface of CMC-AM, suggesting that Cr 6+ was adsorbed on the surface of CMC-AM and then reduced in situ to Cr 3+ . Hence four dominant steps were involved in the removal of Cr 6+ : amino protonation (-NH 3 + ) → adsorption of HCrO 4 - → reduction of HCrO 4 - by -OH group and production of Cr 3+ → desorption of Cr 3+ . Differing with other common disposable adsorbents, CMC-AM resin could self-regenerate active adsorption sites spontaneously via coulomb repulsion between -NH 3 + and Cr 3+ , displaying an intelligent self-generation function. Furthermore, the cyclic test of CMC-AM showed that 86% of Cr 6+ ions were still removed after 6 cycles without any additional chemical treatment, indicating that CMC-AM has a satisfying self-regeneration capability.
engineering, chemical, environmental