Systematic Investigation on the Formation of Honeycomb-Patterned Porous Films from Amphiphilic Block Copolymers
Bai-Heng Wu,Liang-Wei Zhu,Yang Ou,Wen Tang,Ling-Shu Wan,Zhi-Kang Xu
DOI: https://doi.org/10.1021/jp5119212
2015-01-01
The Journal of Physical Chemistry C
Abstract:The breath figure method is a very simple and highly efficient technique to prepare honeycomb-patterned porous structures. Amphiphilic block copolymers are the most used film-forming materials. However, the relationship between block copolymer composition and film morphology is still unknown, which hinders the large-scale fabrication of the films. In this work, we synthesized more than 30 amphiphilic block copolymers with different chemical compositions by atom transfer radical polymerization (ATRP). Honeycomb films were prepared from polystyrene-block-poly(N,N-dimethylaminoethly methacrylate) (PS-b-PDMAEMA) by the breath figure method. An empirical morphology diagram was obtained to show the relationship between the block copolymer composition and the film-forming ability, in which zones corresponding to large-area ordered, ordered, partially ordered, and disordered films have been revealed. Moreover, interfacial tensions of these copolymers were measured by a pendant drop method. A polymerization degree ratio of PDMAEMA block to PS block between 0.01 and 0.02, which has interfacial tensions in the range of 34.546.0 mN/m, is favorable for the preparation of ordered honeycomb films. For polystyrene-block-poly(2-hydroxyethyl methacrylate) (PS-b-PHEMA) that has a more hydrophilic block than PS-b-PDMAEMA, it may form reverse micelles in solutions and hence shows different interfacial tensions and self-assembling behaviors when the PHEMA block is long. This study unveils the relationship between block copolymer composition and honeycomb film morphology and provides new insights into designing polymers for large-area, highly ordered, and reproducible honeycomb-patterned porous films.