Abstract:Defect-engineering of TiO2 materials is an effective way to enhance their light absorption. However, activities in the visible-light region are still far from satisfactory due to the uncontrollable defect location. Herein, we demonstrate a facile confinement reduction route to introduce controllable defects to mesoporous TiO2 micro-spheres with phase junctions (denoted as M-TiO2-PJs) by using sodium borohydride (NaBH4) as the reducing agent. In this case, the confinement decomposition effect of mesopore channels over NaBH4 enables the generation of defects more effectively at a mild reaction condition, enabling the well-retained mesoporous and phase junction structures of mesoporous TiO2 microspheres. Moreover, by changing the reduction temperature, the defects are migrated from the nanocrystalline-exposed surfaces to phase junction interfaces, enabling that the location of the defects can be well-tuned. After the reduction at 300 degrees C, the resultant defective mesoporous TiO2 microspheres show the well-retained mesostructure, high surface areas (similar to 75.6 m(2) g(-1)), large pore volumes (0.36 cm(3) g(-1)), slightly disordered surfaces and intimately contacted anatase-rutile interfaces, which exhibit the state-of-the-art activities for photocatalytic water splitting. The H-2 generation rate is as high as 42.6 mu mol h(-1) (based on 50 mg of catalyst) under visible-light (lambda > 400 nm) and the apparent quantum efficiencies are estimated to be 12.7% and 2.8% at 420 and 520 nm, respectively, which are the best values among TiO2-based photocatalysts reported to date. We also show that the defective mesoporous TiO2 microspheres possess a super CH4 selectivity (57%) and yield (15 nmol h(-1)) for CO2 reduction under visible-light because of the activation and adsorption effect of defects for CO2 molecules. This work provides new insight into rational design of high performance photocatalysts.

Scalable Preparation of Defect-Rich Free-Standing TiO2 Sheets with Visible-Light Photocatalytic Activity

Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets

Surfactant-Free Synthesis of Single-Crystalline Bi4Ti3O12 Nanosheets with Excellent Visible-Light Photocatalytic Activity

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

Single-crystalline Ultrathin 2D TiO2 Nanosheets: A Bridge Towards Superior Photovoltaic Devices

Facile Approach for the Syntheses of Ultrafine TiO2 Nanocrystallites with Defects and C Heterojunction for Photocatalytic Water Splitting

Facile Synthesis of Defective TiO2−x Nanocrystals with High Surface Area and Tailoring Bandgap for Visible-light Photocatalysis

Anatase Tio2 Films with Dominant {001} Facets Fabricated by Direct-Current Reactive Magnetron Sputtering at Room Temperature: Oxygen Defects and Enhanced Visible-Light Photocatalytic Behaviors

A Novel Etching and Reconstruction Route to Ultrathin Porous TiO2 Hollow Spheres for Enhanced Photocatalytic Hydrogen Evolution

Surface Energy-Driven Solution Epitaxial Growth of Anatase TiO2 Homostructures for Overall Water Splitting

Synthesis of monolayer carbon-coated TiO2 as visible-light-responsive photocatalysts

Fabrication and Properties of a Free-Standing Two-Dimensional Titania

Tio2 Nanosheets Synthesized by Atomic Layer Deposition for Photocatalysis

Surface Defect Engineering in Colored TiO2 Hollow Spheres Toward Efficient Photocatalysis

Influence of Ti$_3^+$ Defect-type on Heterogeneous Photocatalytic H$_2$ Evolution Activity of TiO$_2$

Defect-engineering of Mesoporous TiO2 Microspheres with Phase Junctions for Efficient Visible-Light Driven Fuel Production

Combining High Photocatalytic Activity and Stability Via Subsurface Defects in TiO2

A simple sol–gel hydrothermal method for the synthesis of defective TiO2 nanocrystals with excellent visible-light photocatalytic activity

In Situ Tuning of Defects and Phase Transition in Titanium Dioxide by Lithiothermic Reduction

Aerodynamic Levitated Laser Annealing Method to Defective Titanium Dioxide with Enhanced Photocatalytic Performance