Effect of irradiation on temperature performance of dispersion-compensation no-core cascade optical-fiber sensor coated with polydimethylsiloxane film
Fang Wang,Qiu-Feng Wu,Yu-Rong Jiang,Chan Jin,Xiao-Hui Wang,Ben-Shang Zhang,Chun-Wang Ma
DOI: https://doi.org/10.1007/s41365-022-01100-3
2022-09-13
Nuclear Science and Techniques/Hewuli
Abstract:A temperature measurement device can produce data deviations and can even be damaged in a high-dose radiation environment. To reduce the radiation damage to such a device and improve the temperature measurement accuracy in a radiation environment, a temperature sensor based on optical-fiber sensing technology is proposed. This sensor has a cascade structure composed of a single-mode fiber (SMF), a dispersion-compensation fiber (DCF), a no-core fiber (NCF), and another SMF (SDNS). The DCF and NCF are coated with a polydimethylsiloxane (PDMS) film, which is a heat-sensitive material with high thermal optical and thermal expansion coefficients. In experiments, PDMS was found to produce an irradiation crosslinking effect after irradiation, which improved the temperature sensitivity of the SDNS sensor. The experimental results showed that within a range of 30–100 °C, the maximum temperature sensitivity after irradiation was 62.86 pm/°C, and the maximum transmission sensitivity after irradiation was 3.353 × 10 −2 dB/°C, which were 1.22 times and 2.267 times the values before irradiation, respectively. In addition, repeated temperature experiments verified that the SDNS sensor coated with the PDMS film had excellent temperature repeatability. Furthermore, it was found that with an increase in the irradiation intensity, the irradiation crosslinking degree of PDMS increased, and the temperature sensitivity of the sensor was improved. The proposed sensor could potentially be applied to temperature measurement in a nuclear-radiation environment.