Abstract:Gd2 (MoO4 )3 :Eu3+ red phosphors assigned to different crystal systems were prepared using a sol-gel method with ammonium molybdate, Gd2 O3 , and Eu2 O3 as starting materials. X-ray diffraction (XRD) patterns showed that when annealing temperature was 700°C or 800°C, Eu3+ doping concentration was the main factor affecting sample structure. When the Eu3+ doping concentration was 0-2.00 mol%, samples had a monoclinic structure, but when the Eu3+ doping concentration was increased to 4.00-10.00 mol%, the samples changed to a mixed crystal structure (with existence of both monoclinic and orthorhombic structures). When the annealing temperature was increased to 900°C, annealing temperature became the main factor affecting sample structure, that is sample structure did not change with change in Eu3+ doping concentration, and all samples could be assigned to the orthorhombic system. Change in structure also affected the luminescence properties of the samples. Gd2 (MoO4 )3 :Eu3+ phosphors with different crystal systems could be effectively excited by blue light (466 nm wavelength); red light at 614 nm wavelength gave better colour purity and color stability, corresponding to the Eu3+5 D0 →7 F2 transition. Finally, when Eu3+ concentration was 0.02 mol, the luminescence intensity of the orthorhombic system was higher than that of the monoclinic system; when the concentration was 0.04 mol, the luminescence intensity of the mixed system was almost the same as that of the orthorhombic system.

Charge Transfer Transition and Energy Transfer in Eu3+-doped Gd10V2O20

Luminescent Properties of Gd2SiO5powder Doped with Eu3+under VUV–UV Excitation

Luminescence Behavior of the Eu(Ttfa)(3) and Tbssa Co-Doped Xerogel

Study of Eu3+-doped Luminescence Glasses Prepared by a Sol-Gel Process

Photoluminescence Characteristics and Energy Transfer Between Bi3+ and Eu3+ in Gd2o3: Eu3+, Bi3+ Nanophosphors

Energy Transfer in the Luminescence Process of YTaO4: Gd, Eu

Hydrothermal Synthesis and Luminescence Properties of NaGdF4:Eu3+ Crystals

Photoluminescence characteristics and energy transfer between Bi 3+ and Eu 3+ in Gd 2 O 3 : Eu 3+ , Bi 3+ nanophosphors

Spectroscopy analysis and optical transition property of GdNbTiO6: Eu3+, Sm3+ phosphor

Synthesis and Luminescent Properties of Nanoscale Gd2si2o7:Eu3+ Phosphors

Preparation and luminescence properties of Gd2 (MoO4 )3 :Eu3+ red phosphors with high colour purity

Study of Vacuum Ultraviolet and Ultraviolet Excitation Spectra of GdVO4∶Eu 3+

Energy transfer in Sm3+/Eu3+ doped Li6Gd(BO3)3 orange-red phosphor

Energy Transfer Mechanisms in Yb3+-Doped Gdvo4 Near-Infrared Downconversion Nanophosphor

Study on VUV and UV Excitation Spectrum of GdVO 4 ∶eu 3+

Novel Color-Tunable Gd2o2cn2:Tb3+, Eu3+ Phosphors: Characterization and Photoluminescence Properties

Energy Transfer In (Y-0.65,Gd-0.35)Bo3 : Bi-0.01(3+),Eu-0.04(3+) Under Vuv Excitation

Structural and luminescent properties of Eu3+ doped Gd17.33(BO3)4(B2O5)2O16

Luminescence properties of Eu 3+ -doped potassium-gadolinium-phosphate glasses

Suppression of Eu2+ luminescence and enhancement of Eu3+ emission in Eu: CaF2 single crystal via Gd3+ co-doping

Structure transition and enhanced photoluminescence of Gd2-xYxO3:Eu nanocrystals