Abstract:The development of high-speed aerial vehicles urgently requires high-performance integrated materials for ablation resistance, thermal insulation and oxidant protection under high temperature. The previously prepared carbon aerogel composites (C/CA), with ultra-high temperature thermal insulation properties, were impregnated with SiCO precursor sol and pyrolysed in nitrogen atmosphere at 1200?C. The impregnation/pyrolysis process was performed once, twice and thrice to obtain three different C/C-SiCO nanoporous ceramic composites. Further, TaSi2-MoSi2-borosilicate glass (TM-BG) coating or TaSi2-MoSi2-ZrB2-borosilicate glass (TMZBG) coating was prepared on the surface of the C/C-SiCO through slurry brushing combined with graphite powder embedded sintering process. By simulating the actual application environment through oxygen acetylene flame ablation test, the ablation resistance of the samples was studied and their oxidation mechanism was analysed. The results show that the ablation rate of the C/C-SiCO after 200 s ablation at 1600 ?C decreases with the increase of the number of impregnation/pyrolysis steps and that the ablation resistance of the coating modified C/C-SiCO was significantly enhanced. The addition of ZrB2 to the coating improves the compatibility between the substrates and the coating, and the TMZ-BG coated sample has better ablation resistance. At high temperature, the borosilicate glass in the coating is in a viscous flow state. Meanwhile the SiO2 generated by the oxidation of other silicide raw materials forms a dense glass layer on the coating surface, which can be used as an oxygen barrier to provide better protection for the substrates. The coating-modified C/C-SiCO porous ceramic composites are expected to be used as a high-temperature ablation-resistant material for the thermal protection system of new aerospace vehicles.

Ablation behavior of advanced TaSi 2 -based coating on carbon-bonded carbon fiber composite/ceramic insulation tile in plasma wind tunnel

Ablation Experiments of Ultra-High-Temperature Ceramic Coating on Carbon–Carbon Composite Using ICP Plasma Wind Tunnel

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Enhancing Ablation Resistance of TaB2-Based Ultra-High Temperature Ceramics by Mixing Fine TaC Particles and Dispersed Multi-Walled Carbon Nanotubes

Ablation resistance of C/C-SiCo nanoporous ceramic composites with TaSi2-MoSi2-ZrB2-borosilicate glass coating

Ablation Behavior of the SiC-Coated Three-Dimensional Highly Thermal Conductive Mesophase-Pitch-Based Carbon-Fiber-Reinforced Carbon Matrix Composite under Plasma Flame

CMAS Corrosion Resistance Behavior and Mechanism of Hf6Ta2O17 Ceramic as Potential Material for Thermal Barrier Coatings

Ablation mechanism of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC composite during plasma ablation above 2000 °C

Novel Low Thermal Conductivity Ceramic Materials for Thermal Barrier Coatings

Oxidation resistance, ablation resistance and in situ ceramization mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composites modified with Ti3SiC2

Thermal shock performance and failure behavior of Zr6Ta2O17-8YSZ double-ceramic-layer thermal barrier coatings prepared by atmospheric plasma spraying

Progress in ceramic materials and structure design toward advanced thermal barrier coatings

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C

Study on the mechanism of ultra-high temperature ablation of ZrB2–SiC–TaSi2 coatings by low-pressure plasma spraying on the C/C composites

Multiscale structural understanding of plasma spraying anti-ablation coating: an example of Ta-Hf-W-C ultrahigh temperature ceramics

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Novel Thermal Barrier Coatings with Phase Composite Structures for Extreme Environment Applications: Concept, Process, Evaluation and Performance

Ablation behaviors of ultra-high temperature ceramic composites