Ruthenium/nitrogen-doped carbon as an electrocatalyst for efficient hydrogen evolution in alkaline solution

J. Zhang,P. Liu,G. Wang,P. P. Zhang,X. D. Zhuang,M. W. Chen,I. M. Weidinger,X. L. Feng
DOI: https://doi.org/10.1039/c7ta08764k
2017-01-01
Journal of Materials Chemistry
Abstract:For all electrocatalysts (even Pt), the kinetics of the hydrogen evolution reaction (HER) in alkaline environments are more sluggish by a factor of two to three compared to those in acidic solutions. Here, we demonstrated the preparation of a novel ruthenium/nitrogen-doped carbon (Ru/NC) electrocatalyst supported by graphite foam, in which abundant, singly dispersed Ru atoms were chelated to a nitrogendoped carbon matrix. In a 1 M KOH aqueous solution, the resultant Ru/NC electrocatalyst exhibited excellent electrocatalytic HER activity with an extremely low overpotential of only 21 mV at 10 mA cm(-2) and an excellent mass current density as high as 8 A mgRu(-1) at 100 mV, which is superior to the values for reported electrocatalysts (overpotentials of > 50 mV at 10 mA cm(-2)), even Pt catalysts (overpotential of similar to 36 mV at 10 mA cm(-2)). Importantly, the inherent turnover frequency (TOF) value (per Ru atom) of the Ru/NC electrocatalyst reaches 4.55 s(-1), which is 3.2 times higher than that of the Pt catalyst (1.41 s(-1)). Electrochemical analyses and structural characterization revealed that atomically dispersed Ru is responsible for the outstanding HER activity of the Ru/NC electrocatalyst because of a substantially accelerated Volmer step. The outstanding HER performance gives the Ru/NC electrocatalyst promising potential for practical hydrogen production applications.
What problem does this paper attempt to address?